Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 9.20 GPa | 1330 ksi | STN EN ISO 178 |
Plastcom SLOVAMID 66 GF 35 Polyamide 66, 35% Glass Fiber FeaturesChemically reinforced with 35% glass fiber, suitable for mouldings with high strength and toughness also at low temperatures. Used in the automotive, engineering and electrical industry. W.. |
|||
Flexural Modulus | 9.17 GPa | 1330 ksi | ASTM D790 |
LNP Lubricomp® PDX-O-90351 Polyphenylene Sulfide, Glass Fiber Reinforcement, PTFE Lubricant
(discontinued **) Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac.. |
|||
Flexural Modulus | 9.17 GPa | 1330 ksi | ASTM D790 |
Covestro Petlon® 8535 Semi-Crystalline PET, 35% Mineral/Glass Fiber
(discontinued **) Characteristics: Impact Modified: Excellent Electrical Properties, High Heat ResistanceApplications: Automotive (Under Hood), Appliances, Casings and HousingsProcessing: Injection Molding (Melt Temp.. |
|||
Flexural Modulus | 9.17 GPa | 1330 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP OX90351 PPS LNP LUBRICOMP* OX90351 is a compound based on Polyphenylene Sulfide resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. |
|||
Flexural Modulus | 9.14 GPa | 1330 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2310EPR PEI (Europe-Africa-Middle East) 30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. Resin is RoHS compliant. UL94 V0 listing. |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 865 PBT (Europe-Africa-Middle East) VALOX 865 is a 30% glass fibre reinforced, non blooming flame retardant PBT+PET blend with an excellent surface appearance. Applications: External housings, steam irons, appliance housings and light.. |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® ENH4550 PBT (Asia Pacific) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® ENH4550 PBT (Europe-Africa-Middle East) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
Flexural Modulus | 9.18 GPa | 1330 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® IQ4860HR PBT (Europe-Africa-Middle East) Valox iQ* Resin iQ4860HR: Environmentally responsible iQ* PBT resin with 30% Glass reinforcement + UL94 V-0. Hydrolytically stable and impact modified. |
|||
Flexural Modulus | 9.17 GPa | 1330 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP AF006XXZ ABS LNP* THERMOCOMP* AF006XXZ is a compound based on ABS resin containing 30% Glass Fiber. |
|||
Flexural Modulus | 9.14 GPa | 1330 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP PF007 PA 6 LNP* THERMOCOMP* PF007 is a compound based on Nylon 6 resin containing 35% Glass Fiber. |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | ASTM D790 |
Plenco 00732 Melamine-Phenolic, Granular, Compression Molded PLENCO 00732 is a melamine-phenolic copolymer molding compound, exhibiting excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 007.. |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | ASTM D790 |
Plenco 4304 Phenolic, Nodular, Transfer Molded PLENCO 04304 is a heat resistant, mineral filled phenolic molding compound offering improved mechanical strength properties along with excellent dimensional stability. UL recognized under component .. |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | ASTM D790 |
Plenco 4527 Phenolic, Granular, Transfer Molded PLENCO 04527 is a heat resistant, mineral and flock filled phenolic molding compound, offering excellent mechanical strength, and resistance to cracking in a wet-dry environment. UL recognized under.. |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | ISO 178 |
Polyplastics FR-PET® BN3030SD Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Flame retardant, General purpose Information provided by PolyPlastics. |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | ISO 178 |
Polyplastics FR-PET® CN3030SD Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Flame retardant, General purpose Information provided by PolyPlastics. |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | ISO 178-93 |
Wellman Wellamid® GFX1624-BK(PTFE) 30% Glass Fiber Reinforced, Lubricated Nylon 66 Description: Glass Fiber Reinforced, Lubricated Nylon 66Information provided by Wellman. |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | dry; ISO 178 |
DSM Novamid® 1010GH30 NAT PA6-GF30 30% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | dry; ISO 178 |
DSM Novamid® 1013GH30 1 NA/BK701 PA6-GF30 30% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | dry; ISO 178 |
DSM Novamid® 1017GH33 BK701 PA6-GF33 33% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | cond; ISO 178 |
DSM Stanyl® TW200B6 PA46-CF30 30% Carbon Reinforced, Heat Stabilized, Lubricated |
|||
Flexural Modulus | 9.17 GPa | 1330 ksi | ASTM Test |
BASF Ultramid® 8232G HS FR BK-102 25% Glass Filled PA6 (Dry) Ultramid 8232G HS FR BK-102 is a 25% glass fiber reinforced, heat stabilized, flame retardant pigmented black PA6 injection molding compound exhibiting excellent melt stability characteristics. It .. |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | ISO 178 |
BASF Ultramid® A3X2G7 35% Glass Filled PA66 (Dry) Ultramid A3X2G7 is a 35% glass fiber reinforced injection molding PA66 grade with improved flame retardance and enhanced long-term stability. Flame retardant based on red phosphorus; very high stif.. |
|||
Flexural Modulus | 9.20 GPa | 1330 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC (Asia Pacific) LNP* Lubricomp* DFL369XF is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant. |
|||
Flexural Modulus | 9.15 GPa | 1330 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON QEP35M PA6.10 LNP STAT-KON QEP35M is a compound based on Nylon 6/10 resin containing 25% Milled Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Electrically Conductive, Wear Resistant. |