Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 8.75 GPa | 1270 ksi | |
Plastcom SLOVAMID 6/66 GF 30 FRG 5 TS PA6/66, 30% glass fibre, flame retardant FeaturesPA 6 + PA 66 alloy for injection moulding, chemically reinforced with 30 % glass fibre, with halogen and phosphorus free flame retardant. Main features: flammability in accordance with UL 94.. |
|||
Flexural Modulus | 8.75 GPa | 1270 ksi | ISO 178 |
Radici Radiflam® ARV350 AF (dry) Nylon 66 PA66 Self-extinguishing glass-fiber reinforced with phosphorousInformation provided by Radici group. |
|||
Flexural Modulus | 8.76 GPa | 1270 ksi | ASTM D790 |
LNP Thermocomp® LF-1004 Polyetheretherketone, Glass Fiber Reinforcement
(discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names.. |
|||
Flexural Modulus | 8.73 GPa | 1270 ksi | 5 mm/min; ISO 178 |
Gromax BFG30-EN04B2 Nylon 6 36% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Modulus | 8.74 GPa | 1270 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT LNP LUBRICOMP* WFP36 is a compound based on PBT resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant. |
|||
Flexural Modulus | 8.74 GPa | 1270 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT (Asia Pacific) LNP LUBRICOMP* WFP36 is a compound based on Polybutylene Terephalate resin containing Silicone, Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 8.76 GPa | 1270 ksi | ASTM D790 |
Techmer ES Electrablend® ABS CF10 FR BK 10% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightFeatures: Flame RetardantAppearance: BlackInformation provided by TP Composites, Inc. |
|||
Flexural Modulus | 8.79 GPa | 1270 ksi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON DX01303C PC LNP STAT-KON* DX01303C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive. |
|||
Flexural Modulus | 8.73 GPa | 1270 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON REL33 PA 66 LNP STAT-KON* REL33 is a compound based on Nylon 66 resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant. |
|||
Flexural Modulus | 8.75 GPa | 1270 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF006ER PC LNP THERMOCOMP* DF006ER is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release. |
|||
Flexural Modulus | 8.75 GPa | 1270 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP Noryl_PCN2910 PPE+PS LNP* Thermodcomp* Noryl_PCN2910 compound is a 35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market. |
|||
Flexural Modulus | 8.73 GPa | 1270 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF006L PA 66 LNP* THERMOCOMP* RF006L is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Low Extractible. |
|||
Flexural Modulus | 8.73 GPa | 1270 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF006L PA 66 (Asia Pacific) LNP* Thermocomp* RF006L is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Low Extractible. |
|||
Flexural Modulus | 8.73 GPa | 1270 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF006LXP PA 66 LNP* THERMOCOMP* RF006LXP is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Low Extractible. |
|||
Flexural Modulus | 8.78 GPa | 1270 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp RF006PS PA 66 LNP* Thermocomp* RF-1006 EP HS is based on Nylon 6/6 containing Glass Fiber. Characteristics of this grade include Exceptional Processing and Heat Stabilizer.This data was supplied by SABIC-IP for .. |
|||
Flexural Modulus | 8.74 GPa | 1270 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP ZFM62P PPE+PS LNP* THERMOCOMP* ZFM62P is a compound based on PPE+PS resin containing 10% Glass Fiber, 30% Mical. Added features of this material include: Exceptional Processing. |
|||
Flexural Modulus | 8.75 GPa | 1270 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP Noryl_PCN2910 PPE+PS (Asia Pacific) 35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market. |
|||
Flexural Modulus | 8.76 GPa | 1270 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOTUF CF007IXP PS LNP* Thermotuf* CF007IXP is a compound based on Polystyrene containing glass fiber. Characteristics of this grade are: High Impact. |
|||
Flexural Modulus | 8.76 GPa | 1270 ksi | ASTM Test |
BASF Petra® 130 BK-112 30% Glass Filled PET Petra 130 BK-112 is a 30% glass fiber reinforced, black pigmented polyethylene terephthalate injection molding compound. It exhibits a combination of performance properties including good strength .. |
|||
Flexural Modulus | 8.76 GPa | 1270 ksi | ASTM D790 |
Applied Nanostructured Solutions Carbon NanoStructure Chopped Fiber Carbon NanoStructure (CNS) Chopped Fiber begins as a single-end glass roving product, such as E-CR glass, that is enhanced using a proprietary ANS process. Unique multiwall carbon nanotube-based CNS.. |
|||
Flexural Modulus | 8.76 GPa | 1270 ksi | ASTM D790 |
Asahi Kasei Thermylene® P7-45FG-0790 45% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
Flexural Modulus | 8.75 GPa | 1270 ksi | STN EN ISO 178 |
Plastcom SLOVAMID 66/6 GF 30 Polyamide 66/6, 30% Glass Fiber
(discontinued **) FeaturesChemically reinforced alloy PA 66 and PA 6 with 30% glass fiber, suitable for mouldings with high strength and toughness also at low temperatures. Used in the automotive, engineering and el.. |
|||
Flexural Modulus | 8.76 GPa | 1270 ksi | ISO Data |
BASF Petra® 230 BK-112 22/13% Glass/Mineral Filled PET Petra 230 BK-112 is a 35% mineral and glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a very good combination of performance properties in.. |
|||
Flexural Modulus | 8.76 GPa | 1270 ksi | ASTM D790 |
LNP Thermocomp® JF-1006 EM Polyethersulfone, Glass Fiber Reinforcement
(discontinued **) Features: Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are st.. |
|||
Flexural Modulus | 8.76 GPa | 1270 ksi | ASTM D790 |
PlastxWorld CEVIAN® B2706 30% GF PBT/ABS Alloy Glass fiber reinforced PBT/ABS alloy.Information provided by PlastxWorld Inc. |
|||
Flexural Modulus | 8.74 GPa | 1270 ksi | ASTM D790 |
Plenco 50335 PET, Pellet, Injection Molded, Natural Color
(discontinued **) PLENCO 50335 is an engineering grade glass reinforced polyethylene terephthalate resin designed for excellent dimensional stability. It is UL listed and available in white, natural, and black.Inform.. |