Polymer Property : Flexural Modulus = 1170 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	8.10 GPa	1170 ksi
Plastcom SLOVAMID 66 Y 35 FRY 7 PA66, 35% mineral filling FeaturesPA 66 for injection moulding, chemically reinforced with 35 % mineral filler and non-halogen flame retardant, with heat resistance and nonflammability, achieves V 0 /3.2 mm/ in accordance wi..
Flexural Modulus	8.10 GPa	1170 ksi	ISO 178
Radici Radilon® ARV300 (dry) Nylon 66 30% Glass-fiber reinforcedInformation provided by Radici group.
Flexural Modulus	8.10 GPa	1170 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL36E PC (Europe-Africa-Middle East) LNP* LUBRICOMP* DFL36E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features include; Internally Lubricated, Easy Molding.
Flexural Modulus	8.10 GPa	1170 ksi	ASTM D790
Solvay Specialty Polymers Amodel® A-4122 LS WH678 Polyphthalamide (PPA) (Unverified Data**) Amodel A-4122 LS is a 22% glass fiber reinforced, light-stabilized, high-reflectivity white grade of Amodel polyphthalamide (PPA). It is designed to provide high crystallinity when molded in water-c..
Flexural Modulus	8.10 GPa @Temperature 100 °C	1170 ksi @Temperature 212 °F	Conditioned; ISO 178
Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA) (Unverified Data**) Amodel AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both infrar..
Flexural Modulus	8.07 GPa	1170 ksi	ASTM D790
Solvay Specialty Polymers Veradel® AG-230 Polyethersulfone (discontinued **) For superior long-term performance at high temperatures in severe service environments. It offers especially good toughness, hydrolytic stability, chemical resistance, plus FDA and USDA compliance.N..
Flexural Modulus	8.07 GPa	1170 ksi
Phenolic 37%, Graphite fabric 63% Phenolic - "91LD". Graphite fabric - "WCB"
Flexural Modulus	8.04 GPa	1170 ksi	5 mm/min; ISO 178
Gromax BFG30-DN00N1 Nylon 6 30% Glass Filled (Dry) Information provided by Gromax Enterprises Corp.
Flexural Modulus	8.10 GPa @Temperature 100 Â°C	1170 ksi @Temperature 212 Â°F	ISO 178
Solvay Specialty Polymers AmodelÂ® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Conditioned) AmodelÂ® AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both in..
Flexural Modulus	8.07 GPa @Temperature 100 Â°C	1170 ksi @Temperature 212 Â°F	ISO 178
Solvay Specialty Polymers AmodelÂ® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Dry) AmodelÂ® AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both in..
Flexural Modulus	8.10 GPa	1170 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Stat-kon DCL33 PC (Europe-Africa-Middle East) LNP* Stat-kon* DCL4033 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP ..
Flexural Modulus	8.04 GPa	1170 ksi	ISO 178
SABIC Innovative Plastics LNP STAT-KON DE003 PC (Asia Pacific) LNP STAT-KON* DE003 is a compound based on Polycarbonate resin containing Carbon Fiber.
Flexural Modulus	8.04 GPa	1170 ksi	ISO 178
SABIC Innovative Plastics LNP STAT-KON DE003ER PC LNP STAT-KON* DE003ER is a compound based on Polycarbonate resin containing 15% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Statically Conductive.
Flexural Modulus	8.05 GPa	1170 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP GX05482 PSU LNP* THERMOCOMP* GX05482 is a compound based on Polysulfone resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant.
Flexural Modulus	8.08 GPa	1170 ksi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 (Asia Pacific) LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System.
Flexural Modulus	8.04 GPa	1170 ksi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® GP-5300G PBT, Glass Filled Information provided by Samsung Cheil Industries.
Flexural Modulus	8.10 GPa	1170 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RF007SXP PA 66 LNP* THERMOCOMP* RF007SXP is a compound based on Nylon 66 containing 35% Glass Fiber. Added feature of this material includes: Heat Stabilized.
Flexural Modulus	8.05 GPa	1170 ksi	ASTM D790
UBE UBESTA® 3020GX6 Glass Fiber Reinforced Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: conductive, glass fiber reinforced, UV resistanceInformation provided by UBE.
Flexural Modulus	8.10 GPa	1170 ksi	ASTM D790
Plenco 00732 Melamine-Phenolic, Granular, Transfer Molded PLENCO 00732 is a melamine-phenolic copolymer molding compound, exhibiting excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 007..
Flexural Modulus	8.10 GPa	1170 ksi	ASTM D790
Plenco 2000 Phenolic, Granular, Compression Molded PLENCO 02000 is a versatile general purpose, organic filled phenolic molding compound, offering optimum cure characteristics and an excellent balance of molding properties. UL recognized under compo..
Flexural Modulus	8.10 GPa	1170 ksi	ASTM D790
Plenco 2369 Phenolic, Granular, Compression Molded PLENCO 02369 is a general purpose, organic filled phenolic molding compound, formulated to minimize the generation of free ammonia for applications that are sensitive to such formation. PLENCO 02369..
Flexural Modulus	8.10 GPa	1170 ksi	cond; ISO 178
DSM EcoPaXX® Q-X07209 PA410-I-GF40 % Glass Reinforced, Impact Modified
Flexural Modulus	8.10 GPa	1170 ksi	cond; ISO 178
DSM Novamid® 3010GN30 NAT PA66-GF30 FR(17) 30% Glass Reinforced, Flame Retardant
Flexural Modulus	8.10 GPa	1170 ksi	Dry; ASTM D790
Asahi Kasei Leona® 14G25 25% Glass Filled Nylon 66 Enhanced strength and stiffness; with 25% GF. Superior heat aging resistance, fatigue resistance, and creep resistance.Applications:Mechanical and electrical parts, engine mounts and other under-the..
Flexural Modulus	8.04 GPa	1170 ksi	ASTM D790
Gromax CCP PBT 3030-200HR 30% Glass Fiber Filled Product Description: A glass fiber 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent ..
Flexural Modulus	8.07 GPa	1170 ksi	ASTM D790
PolyOne Stat-Tech™ NJ-20CF/000 Black Polyamide 12 (Nylon 12) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound..
Flexural Modulus	8.04 GPa	1170 ksi	5 mm/min; ISO 178
Gromax CFG30-QN11N1 Nylon 6 30% Glass Filled (Dry) Information provided by Gromax Enterprises Corp.