Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.689 GPa | 100 ksi | 1.3 mm/min; ASTM D790B |
Polimeros Mexicanos Rotolene® 93050 Medium Density Polyethylene Hexene Copolymer Linear Medium Density Polyethylene for rotational molding. This resin is fully UV8 stabilized.Recommended for general purpose applications. Frequently used for water tanks (less tha.. |
|||
Flexural Modulus | 0.689 GPa | 100 ksi | 1.3mm per min; ASTM D790 |
Formosa Plastics Formolene® L63550U Rotational Molding LLDPE
(discontinued **) Hexene CopolymerApplications: Toys, medium tanks, material handling equipment and flat surface rotational molding applications.Formolene L63550 is fully heat and UV stabilized.Meets all requirements.. |
|||
Flexural Modulus | 0.690 GPa | 100 ksi | ASTM D790 |
Chevron Phillips Marlex® CL-200YB (Black) Rotational molding crosslinkable high density polyethylene
(discont Benefits: crosslinks during molding - has outstanding melt strength at 204°C, is formulated to provide maximum UV protection for long-term outdoor weathering, contains an internal mold release, exc.. |
|||
Flexural Modulus | 0.690 GPa | 100 ksi | at 1% elongation; ASTM D790 |
Petromont 2100 Medium Density Polyethylene Resin Petromont HDPE 2100 is a medium density polyethylene blown film resin produced using the UNIPOL™ Process. This resin is designed specifically for blown film made by co-extrusion. It is commonly use.. |
|||
Flexural Modulus | 0.690 GPa | 100 ksi | 1.3 mm/min; ASTM D790 |
ICO Polymers ICORENEâ„¢ 115-1325 LMDPE Rotational Molding Resin Description: ICORENE 115-1325 is a linear medium density polyethylene developed for use in rotational molding. It is an easy processing material with good surface gloss, scratch resistance and gene.. |
|||
Flexural Modulus | 0.690 GPa | 100 ksi | ASTM D747 |
Ineos B50-35H-176 HDPE B50-35H is a high density polyethylene copolymer developed for blow molding. It is recommended for use in applications which require a combination of high top load strength and good environmental s.. |
|||
Flexural Modulus | 0.690 GPa | 100 ksi | ASTM D747 |
Ineos B54-25H-127 HDPE B54-25H-127 is a high density polyethylene copolymer developed for blow molding. It is recommended for use in applications which require a combination of high top load strength and good environmenta.. |
|||
Flexural Modulus | 0.690 GPa | 100 ksi | ASTM D 790 |
Ineos K38-20X2091 HDPE K38-20X2091 is a yellow medium density polyethylene resin designed specifically for natural gas pipe extrusion. It exhibits excellent long term stress life and slow crack growth resistance. This m.. |
|||
Flexural Modulus | 0.689 GPa | 100 ksi | 2% Secant-Method 1; ASTM D790 |
Ineos TUB 172 HDPE TUB 172 is a yellow medium density polyethylene copolymer designed specifically for the extrusion of natural gas pipe. It exhibits excellent long term stress life and slow crack growth resistance. T.. |
|||
Flexural Modulus | 0.690 GPa | 100 ksi | ISO 178 |
Solvay TECHNYL® eXten D 458P PA6.10, DRY Description: Product in development - provisional datasheet. High viscosity unfilled plasticized PA6.10 for extrusion applications providing low end part warpage.Available in: Asia Pacific, Europe, .. |
|||
Flexural Modulus | 0.689 GPa | 100 ksi | ASTM D790 |
ScanTube PFA Tubing Information provided by ScanTube, Inc. |
|||
Flexural Modulus | 0.689 GPa | 100 ksi | ASTM D790 |
A. Schulman POLYTROPE™ TPP 1010-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristics .. |
|||
Flexural Modulus | 0.689 GPa | 100 ksi | ASTM D790 |
A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010HF-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristic.. |
|||
Flexural Modulus | 0.689 GPa | 100 ksi | at 1% secant; ASTM D790 |
A. Schulman SCHULINK® X XL350 Cross-Linkable, High Density Polyethylene DescriptionSchuLink XL 350 is a cross-linkable, high density polyethylene used from rotational molding. This resin offers high impact strength, good abrasion resistance, good stiffness, and excelle.. |
|||
Flexural Modulus | 0.690 GPa | 100 ksi | tangent; ASTM D790 |
A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Flexural Modulus | 0.689 GPa | 100 ksi | ASTM D790 |
A. Schulman POLYTROPE™ TPP 1010E-01 Olefinic Elastomer For Sheet Extrusion DescriptionPolytrope TPP 1010E-01 is an olefinic elastomer designed for sheet extrusion, profile extrusion and blow molding. TPP 1010E-01 is a natural product which can be colored and UV stabilized.. |
|||
Flexural Modulus | 0.689 GPa | 100 ksi | ASTM D790 |
A. Schulman POLYTROPE™ CB 1010U-330 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope CB 1010U-330 is a color matched/color blended injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properti.. |
|||
Flexural Modulus | 0.689 GPa | 100 ksi | ASTM D790 |
A. Schulman POLYTROPE™ TPP 1010-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristics .. |
|||
Flexural Modulus | 0.690 GPa | 100 ksi | ASTM D790 |
Dalau Dalcon 001 100% Virgin PTFE Applications & Industries:General: The static and dynamic friction coefficient are numerically equal, consequently no ’Stick Slip’ occurs.Chemical: Dynamic & shaft seals; Pipes & tubing for carryi.. |
|||
Flexural Modulus | 0.690 GPa | 100 ksi | ASTM D790 |
Dalau Dalcon 020 Virgin PTFE, Carbon (Anti-Static) Applications & Industries: General: The static and dynamic friction coefficient are numerically equal, consequently no ’Stick Slip’ occurs. Electrical: Ideal for Anti - Static Applications; Anti -.. |
|||
Flexural Modulus | 0.689 GPa | 100 ksi | 1% secant; ASTM D790 |
ExxonMobil LLP8555.25 Rotational Molding Resin Product Description: LL 8555 is a linear low density hexene copolymer designed to offer superior processability, excellent dimensional control, whiteness and low warpage. This resin is ideally suite.. |
|||
Flexural Modulus | 0.689 GPa | 100 ksi | ASTM D790 |
Aaron Industries AAROLENE® ARPE HD 300-2 High Density Polyethylene Compounded Resin AAROLENE® ARPE 300 Series Polyethylene Compounded Resin HDPEColor may be specified. Melt Flow Index may be specified. Specific Gravity may be specified. |
|||
Flexural Modulus | 0.690 GPa | 100 ksi | ASTM D790 |
Ashley Polymers Ashlene® 847 Nylon 6, Film Grade A very high impact, low flexural modulus Nylon 6 resin for molding or extrusion. Outstanding low temperature properties.Data provided by the manufacturer |
|||
Flexural Modulus | 0.689 GPa | 100 ksi | ASTM D790 |
Multibase Multi-Flam™ 0107 HDPE Polyethylene Features:Flame RetardantHalogen Content, Low to None Forms:PelletsProcessing Methods:Injection MoldingCoextrusionExtrusionUses:TubingPipingInformation provided by Multibase |