Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 9.85 GPa | 1430 ksi | |
Plastcom SLOVAMID 66 GF 25 FRA 5 PA66, 25% glass fibre, flame retardant FeaturesPA 66 for injection moulding, reinforced with 25% glass fibre and halogen flame retardant. Application in electrical industry: breakers, coilforms, covers, terminals. Slightly decreased flam.. |
|||
Flexural Modulus | 9.85 GPa | 1430 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC3008A PPE+HIPS (Europe-Africa-Middle East) LNP* Stat-kon* Noryl_HMC3008A compound is a 30% glass/mineral/carbon fiber reinforced resin; static dissipative; 250F (120C) HDT. Tight tolerance molding. |
|||
Flexural Modulus | 9.85 GPa | 1430 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC3008A PPE+PS LNP* Stat-kon* Noryl_HMC3008A compound is a 30% glass/mineral/carbon fiber reinforced resin; static dissipative; 250F (120C) HDT. Tight tolerance molding. |
|||
Flexural Modulus | 9.85 GPa | 1430 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON RE004MPC PA 66 LNP* STAT-KON* RE004MPC is a compound based on Nylon 66 resin containing 20% Milled Carbon Fiber. Added features of this material are: Exceptional Processing, Clean Compound System, Electrically C.. |
|||
Flexural Modulus | 9.85 GPa | 1430 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP LC003E PEEK LNP THERMOCOMP* LC003E is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive |
|||
Flexural Modulus | 9.85 GPa | 1430 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP LC003E PEEK (Asia Pacific) LNP THERMOCOMP* LC003E is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Modulus | 9.85 GPa | 1430 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF PF008IR PA 6 LNP* Thermotuf* PF008IR is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High Impact, Mold Release. |
|||
Flexural Modulus | 9.85 GPa | 1430 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF PF008IR PA 6 (Asia Pacific) LNP* Thermotuf* PF008IR is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High Impact, Mold Release. |