Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 7.92 GPa | 1150 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DFL16E PC LNP* Lubricomp* DFL16E is a compound based on Polycarbonate resin containing 30% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated, Easy Molding. |
|||
Flexural Modulus | 7.92 GPa | 1150 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DFL16E PC (Asia Pacific) LNP* Lubricomp* DFL16E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Easy Molding. |
|||
Flexural Modulus | 7.92 GPa | 1150 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP IFL36 PA6.12 LNP LUBRICOMP* IFL36 is a compound based on Nylon 6/12 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. |
|||
Flexural Modulus | 7.92 GPa | 1150 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP REL22 PA 66 LNP* LUBRICOMP* REL22 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Electrically Conductive. |
|||
Flexural Modulus | 7.92 GPa | 1150 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP SFP36 PA12 LNP* LUBRICOMP* SFP36 is a compound based on Nylon 12 resin containing 30% Glass Fiber 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
Flexural Modulus | 7.92 GPa | 1150 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP XFL36 AMORPHOUS POLYAMIDE LNP* LUBRICOMP* XFL36 is a compound based on Amorphous Nylon containing 30% Glass Fiber and 15% PTFE. Added feature of this material is: Wear Resistant. |
|||
Flexural Modulus | 7.92 GPa | 1150 ksi | 6.4 mm; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM4025 PPE+HIPS (Europe-Africa-Middle East) LNP* Thermocomp* Noryl_FM4025 compound is GR/MR 40%, high modulus structural foam. 10% weight reduction, 0.250"" wall thickness. |
|||
Flexural Modulus | 7.92 GPa | 1150 ksi | 6.4 mm; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM4025 PPE+PS LNP* Thermocomp* Noryl_FM4025 compound is GR/MR 40%, high modulus structural foam. 10% weight reduction, 0.250"" wall thickness. |
|||
Flexural Modulus | 7.92 GPa | 1150 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON LX00797C PEEK LNP* STAT-KON* LX00797C is a compound based on Polyetheretherketone containing Proprietary Filler(s). Added features of this material include: ristics of this grade are: Clean Compounding System, .. |