Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 7.55 GPa | 1100 ksi | ASTM D790 |
Kotec Carbotex KG-30MRA Polycarbonate, 30% Glass Fiber Reinforced Features: Glass fiber 30% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E .. |
|||
Flexural Modulus | 7.55 GPa | 1100 ksi | ASTM D790 |
Kotec Carbotex KGN-30MRA Polycarbonate, Flame Retardant, 30% Glass Fiber Reinforced Features: Glass fiber 30% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E .. |
|||
Flexural Modulus | 7.55 GPa | 1100 ksi | 5 mm/min; ISO 178 |
Gromax BFM40-DL04N1 Nylon 6 40% Mineral Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Modulus | 7.55 GPa | 1100 ksi | 5 mm/min; ISO 178 |
Gromax BFG30-BN00B2 Nylon 6 33% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Modulus | 7.55 GPa | 1100 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® TK-2046HM PCT, 40% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 7.55 GPa | 1100 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp OK006 PPS - Linear LNP* Thermocomp* OK006 is based on a Linear Polyphenylene Sulfide (PPS) containing Talc.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 7.55 GPa | 1100 ksi | ISO 178 |
BASF Ultramid® B3GM35 BK 60564 40% Glass/Mineral Filled PA6 (Dry) Description: Ultramid B3GM35 BK60564 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade.Applications: industrial articles requiring medium rigidity and.. |
|||
Flexural Modulus | 7.55 GPa | 1100 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® TK-2046HM PCT, 40% Glass Filled Information provided by Samsung Cheil Industries. |