Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 6.27 GPa | 910 ksi | ASTM D790 |
Quadrant EPP Semitron® 420 ESd V (ASTM Product Data Sheet) |
|||
Flexural Modulus | 6.27 GPa | 909 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY DF2041 PC LNP LUBRILOY* DF2041 is a compound based on Polycarbonate resin containing 20% Glass Fiber, Proprietary Lubricant. Added features include: Flame Retardant. |
|||
Flexural Modulus | 6.27 GPa | 909 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY DF2041 PC (Asia Pacific) LNP LUBRILOY* DF2041 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant, Glass Fiber. Added features of this material include: Flame Retardant. |
|||
Flexural Modulus | 6.27 GPa | 909 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF004E PC LNP THERMOCOMP* DF004E is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Modulus | 6.27 GPa | 909 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP ZF004 PPE+PS LNP THERMOCOMP* ZF004 is a compound based on PPE+PS resin containing 20% Glass Fiber. |
|||
Flexural Modulus | 6.27 GPa | 909 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF008S PA 66 LNP* THERMOCOMP* RF008S is a compound based on Nylon 6/6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Modulus | 6.27 GPa | 909 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RX05494 PA 66 LNP* Thermocomp* RX05494 is a compound based on Nylon 6/6 resin containing glass fiber fillers. Added features of this material include: Heat Stabilized. |
|||
Flexural Modulus | 6.27 GPa | 910 ksi | ASTM D790 |
Techmer ES HiFill FR® PA6/6 GF20 FR 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 20% Filler by WeightFeatures: Flame RetardantInformation provided by TP Composites, Inc. |