Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
LATI LARIL 13 G/20-V1 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
Flexural Modulus | 6.00 - 21.0 GPa | 870 - 3050 ksi | Average value: 9.46 GPa Grade Count:32 |
Overview of materials for Phenolic, Novolac, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral Filled". Each property range of values reported is minimum and maximum values.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | |
Lehmann & Voss LUVOCOM® 1-8181 Polyamide 66, with carbon fiber, toughness-modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; impact resistance.Reduced moment of inertia compared with metal parts.Elec.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | |
Lehmann & Voss LUVOCOM® 50-7814/EM Polycarbonate, with glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | |
Lehmann & Voss LUVOCOM® 65-8452-2 PP-copolymer, with carbon fiber, aramid reinforcement, lubricant modified Applications: Office communication.Strong, stiff parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Dynamic stressed parts.Information provided by.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | 1.3 mm/min; ASTM D790 |
Lavergne VYPET VNT 615 HP PET 15% Glass Reinforced Vypet VNT 615HP is a modified 15% fiberglass reinforced PET injection molding compound designed for automotive structural applications.Features: Easy, fast processing; Excellent strength and stiffne.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | |
Lehmann & Voss ELECTRAFIL M-2386 Polycarbonate, with carbon fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Electrically conductive, suitable for cont.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | |
Lehmann & Voss LUVOCOM® 1-7701 Polyamide 66, with glass fiber and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.Bearings, .. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | |
Lehmann & Voss LUVOCOM® 50/CF/5/GF/10 Polycarbonate, with carbon fiber and glass fiber Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM 2312 PEI (Europe-Africa-Middle East) 30% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF004RXP PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004RXP is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp MX88073 PP (Asia Pacific) LNP* Thermocomp* MX88073 is a compound based on Polypropylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS (Asia Pacific) Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY PF306 PA 6 LNP* STAT-LOY* PF306 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added feature of this grade includes: Antistat. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp MX88073 PP LNP* Thermocomp* MX88073 is a compound based on Polypropylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
A. Schulman POLYFORT™ FXP 6630 Nylon 6.6 Polypropylene Alloy DescriptionPolyfort® FXP 6630 is a nylon 6.6 / polypropylene alloy with 30% wollastonite.Information provided by A. Schulman. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM-D790 |
Polyram RamSter PE300J6 PET, 30% Glass Fiber and Glass Bead Reinforced 30% Glass-fiber and glass beads reinforced, high stiffness PET for injection molding applications.Information provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM-D790 |
Polyram Polytron P35B03 Copolymer Polypropylene, Chemically Coupled 35% Long Glass Fiber A CHEMICALLY COUPLED 35% LONG GLASS FIBERS REINFORCED BLACK POLYPROPYLENE, HEAT STABILIZED FOR INJECTION MOLDING APPLICATION.Information provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D 790 |
Cossa Polimeri ESTAPROP H 0560 GF Polypropylene, 30% Glass Filled PP homopolymer 30% glass fiber reinforcedGood physical and mechanical characteristicsInformation provided by Cossa Polimeri S.r.l. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D 790 |
Cossa Polimeri ESTAPROP H 1660 GFC Polypropylene, 30% Glass Filled PP homopolymer 30% chemically coupled glass fiber reinforcedHigh melt flow rate, excellent impact strengthInformation provided by Cossa Polimeri S.r.l. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
Covestro Bayblend® T 88-4N Polycarbonate/ABS Blend, 20% Glass Fiber Contains 20% glass fiber reinforcement, high stiffness.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – .. |
|||
Flexural Modulus | >= 6.00 GPa | >= 870 ksi | IEC 1212-2 5.2 |
Hippe EP CP 201 Cellulose Paper Reinforced Epoxy Resin - Sheet Used in electronic applications. Good stability of electrical properties under high humidity. Flame retardant.Information provided by Hippe. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | 2 mm/min; ISO 178 |
Eurostar Staramide AG3K PA66, 15% Glass Filled, Injection Molded AG3K is a Heat and Hydrolytically Stabilized, 15% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive suppl.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
Eurostar Staramide RF004EU PA66/6, 20% Glass Fiber Filled, Injection Molded Staramide RF004EU is a 20% Glass Fiber Reinforced Polyamide 66/6 Injection Molding (also known as Staramide 66C 20V S4)Information provided by Eurostar. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | 2 mm/min; ISO 178 |
Eurostar Staramide AG3 PA66, 15% Glass Filled, Injection Molded AG3 is a 15% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
CENTROPLAST CENTROPHEN GF Polyphenylene ether 30% glass fiber This material is a lightweight plastic with low moisture absorption, and is impact resistant at low temperatures. Applications include electronic housings, valve pistons, and support rollers.Inform.. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON PX05047 PA 6 (Europe-Africa-Middle East) LNP* Stat-kon* PX05047 is a compound based on PA 6 resin containing Carbon Fiber, Proprietary Filler (s). Added features include: Electrically Conductive, High Impact. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP GF004 PSU (Asia Pacific) LNP* Thermocomp* GF004 is a compound based on Polysulfone resin containing Glass Fiber. |
|||
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
Beijing Ranger Chem PBT-201-G0 211 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |