Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
Nylene® Norpex® AX20GF , 20% Glass Reinforced Polyphenylene Ether Description: Norpex® AX20GF us a 20% glass fiber reinforced Polyphenylene Ether. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric.. |
|||
Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
Oxford Polymers 15GF 15% Glass Fiber Reinforced Polybutylene Terephthalate (PBT) 15% Glass Fiber Reinforced Polybutylene Terephthalate (PBT)Information provided by Oxford Polymers. |
|||
Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
PolyOne Lubri-Tech™ AS-20GF/05T Acrylonitrile Butadiene Styrene (ABS), Glass Filled, PTFE Lubricated
(discont Description/Features:Glass Fiber ReinforcedPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Flexural Modulus | 4.83 - 19.3 GPa | 700 - 2800 ksi | Average value: 9.22 GPa Grade Count:21 |
Overview of materials for Polycarbonate, NCG Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, NCG Filled". Each property range of values reported is minimum and maximum values of appr.. |
|||
Flexural Modulus | 4.83 - 8.96 GPa | 700 - 1300 ksi | Average value: 6.48 GPa Grade Count:15 |
Overview of materials for Polyetherimide (PEI), 20% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 20% Glass Fiber". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Flexural Modulus | 4.83 GPa | 700 ksi | Tangent; ASTM D790 |
Fiberfil® J-60/30/E4 Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics |
|||
Flexural Modulus | 4.83 GPa | 700 ksi | Tangent; ASTM D790 |
Fiberfil® J-60/30/E8 Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics |
|||
Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
Techmer ES HiFill® HDPE E GF40 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightProcessing Method: ExtrusionInformation provided by TP Composites, Inc. |
|||
Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
Techmer ES HiFill® PA6/6 GF15 L 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by Weight Additive: LubricantFeatures: LubricatedAppearance: Natural ColorInformation provided by.. |
|||
Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
Techmer ES Luriblend® PA6/6 GF10 TL10 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(5%)Features: Lubricated, Good Wear Resistance, Low Fricti.. |
|||
Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
Techmer ES HiFill FR® PA6 GF13 FR 13% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 13% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Flame Retardant, Heat Stabilized and Lu.. |
|||
Flexural Modulus | 4.83 GPa | 701 ksi | Method I (3 point load), 2.0 mm/min; ASTM D790 |
Styron CALIBREâ„¢ 5201-8 Polycarbonate Resin Overview: CALIBREâ„¢ 5201-8 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALIB.. |
|||
Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
Chase Plastics CP Pryme® N130GL (COND, 50% RH) Nylon 6, 30% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
Ensinger Tecapeek® XP-113 Compression Molded PEEK Compound, 10% PTFE, 15% Graphite, and 3% Carbon Fiber Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
Clariant Renol 66B40 Nylon 66, 40% Glass Bead Filled Data provided by Clariant Masterbatches |
|||
Flexural Modulus | 4.83 GPa | 701 ksi | ASTM Data |
BASF Capron® HPN 9315G Impact Modified, 15% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9315G is a 15% glass reinforced, impact modified polyamide 6 injection molding grade resin in the High Productivity Nylon Series developed for applications requiring superior dry-as-molde.. |
|||
Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
PolyOne Edgetek® ATH-15GF/000 Acetal-Homopolymer, Glass Filled
(discontinued **) Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Flexural Modulus | 4.83 - 8.27 GPa | 700 - 1200 ksi | Average value: 7.02 GPa Grade Count:18 |
Overview of materials for Polyphenylene Ether, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 30% Glass Filled". Specific grades with glass content between 25% and 34% are inclu.. |
|||
Flexural Modulus | 4.83 GPa @Temperature 22.8 °C |
700 ksi @Temperature 73.0 °F |
ASTM D790 |
Quadrant EPP Duratron® U2200 PEI Extruded 20% Glass Reinforced Polyetherimide |