Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 4.30 GPa | 624 ksi | STN EN ISO 178 |
Plastcom SLOVAMID 66 GF 15 002/1M PA66 reinforced with glass fiber PA66 for injection molding, reinforced with 15 % glass fiber, for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools,.. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Opnyl OP66GF15 Nylon 66, 14% Glass Reinforced Nylon 66 - Glass reinforced (14 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared.. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ASTM D790 |
NHEP Spectron™ E6046 Nylon 6, 15% Glass Fiber Natural color. E6046 exhibits high rigidity and mechanical strength. It is suitable for wide range of applications. Property data measured at room temperature, 50% RH.Information provided by Bieglo.. |
|||
Flexural Modulus | 4.30 GPa @Temperature 90.0 °C |
624 ksi @Temperature 194 °F |
ISO 178, ASTM D790 |
Nilit Nilamid A G5 FR PH1 25% Glass Fiber Reinforced, Flame Retardant PA66 Description: Nilamid A G5 FR PH1 combines flame retardancy with outstanding mechanical performance. This product has a complete yellow card, with RTI and CTI listings. The formulation has been optim.. |
|||
Flexural Modulus | 4.30 GPa @Temperature 23.0 °C |
624 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPH GF5020 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178 |
Nilit FRIANYL A63 H-SG50 Nylon 6.6 for injection molding, 50% mineral filled Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® RCM6123 PC+ABS (Asia Pacific) Cycoloy* RCM6123 resin is an injection moldable filled PC/ABS blend with non-brominated and non-chlorinated flame retardant. It contains 30% post consumer recycle content with a UL-94 V0 rating @ 1.. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ASTM D790 |
LATI LATILUB 88/50-30GRT PEEK Based, 30% Graphite and PTFE Self Lubricating Plastic
(Unverified Data**)&l Latilub self-lubricating plastic materials are designed to replace metals in applications such as gears, bushings, cams, slides, etc., for which, besides their intrinsic properties (moldability, low.. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178 |
Solvay Specialty Polymers Amodel® AP-9240 NL Polyphthalamide (PPA) Resin, 40% Mineral Filled, Dry as Molded
( AMODEL AP-9240 NL resin is a 40% mineral-filled, impact-modified polyphthalamide (PPA). It was designed to provide a smooth molded surface suitable for many decorative applications. This resin offer.. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178 |
Nilit FRIANYL B63 FK 1010 Nylon 6 for injection molding, 10% glass fiber and 10% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® FL920 PC (Europe-Africa-Middle East) LEXAN FL920 is a foamable grade of LEXAN polycarbonate, containing 20% glass-fibre is designed of applications where superior flexural and tensile charasterics are required. LEXAN FL920 also offers .. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL V03505 PPE+HIPS Noryl* V03505 is a 35% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL V03505 PPE+HIPS (Europe-Africa-Middle East) Noryl* V03505 is a 35% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178 |
SABIC Innovative Plastics LNP Stat-kon KS302 Acetal Copoly LNP* Stat-kon* KS302 is a compound based on Acetal Copolymer resin containing Stainless Steel.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 4.30 GPa @Temperature -30.0 °C |
624 ksi @Temperature -22.0 °F |
1.3 mm/min, 50 mm span, method 1, tangent; ASTM D790 |
A. Schulman POLYFORT™ FTP 3130H-01/FTP 3130HU-Colors DescriptionPolyfort® FTP 3130H-01 (non-UV stabilized) and FTP 3130HU-Colors (UV-stabilized) are high flow injection molding polyolefin alloys which exhibit an exceptional stiffness-impact balance a.. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178-93 |
Wellman Wellamid® FRGS25-6-NBK3 25% Glass Sphere Reinforced Flame Retardant Nylon 66 Description: Glass Sphere Reinforced Flame Retardant Nylon 66Information provided by Wellman. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178-93 |
Wellman Wellamid® GF1701-N1 5% Glass Fiber Reinforced, Engineering Grade Nylon 66 Description: Glass Fiber Reinforced, Engineering Grade Nylon 66Information provided by Wellman. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178-93 |
Wellman Wellamid® GFT1525-BK 15% Glass Fiber Reinforced, Impact Modified Nylon 6 Description: Glass Fiber Reinforced, Impact Modified Nylon 6Information provided by Wellman. |
|||
Flexural Modulus | 4.30 GPa @Temperature -30.0 °C |
624 ksi @Temperature -22.0 °F |
1.3 mm/min, 50 mm span, method 1, tangent; ASTM D790 |
A. Schulman POLYFORT™ FTP 3130H-01/FTP 3130HU-Colors DescriptionPolyfort® FTP 3130H-01 (non-UV stabilized) and FTP 3130HU-Colors (UV-stabilized) are high flow injection molding polyolefin alloys which exhibit an exceptional stiffness-impact balance a.. |
|||
Flexural Modulus | 4.30 GPa @Temperature -30.0 °C |
624 ksi @Temperature -22.0 °F |
1.3 mm/min, 50 mm span, method 1, tangent; ASTM D790 |
A. Schulman POLYFORT™ FTP 3130H-01/FTP 3130HU-Colors DescriptionPolyfort® FTP 3130H-01 (non-UV stabilized) and FTP 3130HU-Colors (UV-stabilized) are high flow injection molding polyolefin alloys which exhibit an exceptional stiffness-impact balance a.. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178 |
Unitika TERRAMAC TE-2000 Polylactic Acid (PLA) Basic grade, Injection grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ASTM D790 |
Unitika UM-8430RG Characteristics: High dimensional accuracy (circularity and planarity) Large warping resistance Low linear expansion coefficientInformation provided by Unitika Ltd. |
|||
Flexural Modulus | 4.30 GPa @Temperature -30.0 °C |
624 ksi @Temperature -22.0 °F |
1.3 mm/min, 50 mm span, method 1, tangent; ASTM D790 |
A. Schulman POLYFORT™ FTP 3130H-01/FTP 3130HU-Colors DescriptionPolyfort® FTP 3130H-01 (non-UV stabilized) and FTP 3130HU-Colors (UV-stabilized) are high flow injection molding polyolefin alloys which exhibit an exceptional stiffness-impact balance a.. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ASTM D 790 |
Cossa Polimeri ESTAPROP H 0540 GFC Polypropylene, 20% Glass Filled PP homopolymer 20% chemically coupled glass fiber reinforcedInformation provided by Cossa Polimeri S.r.l. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | 2 mm/min; ISO 178 |
Eurostar Starflam MF0044 PP, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam MF0044 is a Halogen Free Flame Retardant, Glass Fiber Reinforced, PP Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ASTM D790 |
Adell ER-14 Homopolymer Polypropylene, 20% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ASTM D790 |
Adell ER-34 Homopolymer Polypropylene, 20% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ASTM D790 |
Ashley Polymers Ashlene® 1420B Polycarbonate, 20% Glass Reinforced A 20% glass reinforced polycarbonate for increased mechanical strength and thermal properties, modified for good impact with increased dimensional stability and overall toughness. 1423B with UV sta.. |
|||
Flexural Modulus | 4.30 GPa | 624 ksi | ASTM D790 |
A. Schulman ComAlloy Comtuf® 611 Nylon 6, Glass Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.13% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
Flexural Modulus | 4.30 GPa @Temperature 23.0 °C |
624 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPH GF10020 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |