Polymer Property : Flexural Modulus = 2.759 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	2.759 GPa	400.2 ksi	Method 1, Proc. B; ASTM D-790-95
Multibase Multi-Pro® 2005 XRC Black 20% Filler Content Polypropylene Multi-Pro 2005 XRC is specifically designed for injection molded electronic industrial uses. This product shows higher heat distortion and notched izod than typical glass filled polypropylene. Thi..
Flexural Modulus	2.759 GPa	400.2 ksi	ASTM D790
Ineos Nova 4214 Medium Impact Polystyrene (discontinued **) Excellent balance of properties, USP Class VIApplications: Consumer electronics, Injection molding applicationsProperties were determined on injection molded specimens at 23°C and 50% R.H. unless o..
Flexural Modulus	2.759 GPa	400.1 ksi	ASTM D790
Lucent Polymers 6-01 Nylon 6, General Purpose, Injection Grade Add "R" for Added ReleaseAdd "U" for UV StabilizedTypical Properties, Dry as MoldedInformation provided by Lucent Polymers, Inc.
Flexural Modulus	2.759 GPa	400.1 ksi	ASTM D790
Lucent Polymers CPP-140 Polypropylene Homopolymer, 40% Calcium Carbonate Filled Melt Flow Adjustable for ApplicationAdd "U" for UV StabilizedAdd "H" for Heat StabilizedInformation provided by Lucent Polymers, Inc.
Flexural Modulus	2.759 GPa	400.1 ksi	ASTM D790
Lucent Polymers PBT-310 Polybutylene Terephthalate, 30% Glass Fiber/Mineral Reinforced, Low Warp Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc.
Flexural Modulus	2.759 GPa	400.1 ksi	ASTM D790
Lucent Polymers PBT-FR310 Polybutylene Terephthalate, Flame Resistant Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc.
Flexural Modulus	2.759 GPa	400.2 ksi	ASTM D790
Ineos Nova 4210 Medium Impact Polystyrene (discontinued **) Excellent balance of properties, USP Class VIApplications: Consumer electronics, Injection molding applicationsProperties were determined on injection molded specimens at 23°C and 50% R.H. unless o..