Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.91 GPa | 277 ksi | ASTM D790 |
PolyOne Geon™ HTX Ultra LA426 Gray 2382 Polyvinyl Chloride Alloy (PVC Alloy) Optimum for Black and Darker Colors between 50 and 70 L value. Also suitable for colors above 70 L value.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical propert.. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | 13 mm/min; ASTM D790 |
PolyOne Geon™ L4605 Green 5765 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid) Information provided by PolyOne |
|||
Flexural Modulus | 1.91 - 8.27 GPa | 277 - 1200 ksi | Average value: 2.54 GPa Grade Count:66 |
Overview of materials for Polycarbonate, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Impact Modified". Each property range of values reported is minimum and maximum values of.. |
|||
Flexural Modulus | 1.91 GPa @Thickness 6.40 mm |
277 ksi @Thickness 0.252 in |
10mm/min; ASTM D790 |
LG Chemical LUPOL HF5157Z PP+Rubber+MF, High Flow and Stiffness, High Impact Description: Injection Molding, PP+Rubber+MF, High Flow and Stiffness, High Impact, Good PaintabilityApplication: Automotive Exterior (Slim wall Bumper Fascia)Information provided by LG Chemical |
|||
Flexural Modulus | 1.91 GPa @Thickness 3.20 mm |
277 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOY MP5000AM PC/ABS Description: Injection Molding, PC/ABS, General Purpose, Metal PlatingApplication: Automotive (Exterior), E&E (Housing)CAS: 103598-77-2 and 9003-56-9Information provided by LG Chemical |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Lubricomp IP003 PA6.12 LNP* Lubricomp* IP003 is a Nylon 6/12 base resin containing PTFE and Silicone.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP VN001 Super Tough Nylon LNP* LUBRICOMP* VN001 is a compound based on Super Tough Nylon containing 2% MOS2. Added feature of th is grade is: Wear Resistant. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® TP-1020 PC, Unreinforced Transparent Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SR-7300 ABS/PET, Unreinforced Material with superior chemical resistance that can be used in the interior/exterior material of household appliances that require heat resistanceInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® WP-1041G PC/ABS, Unreinforced Metal Plating Grade Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SR-7300 ABS/PET, Unreinforced Material with superior chemical resistance that can be used in the interior/exterior material of household appliances that require heat resistanceInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | ASTM D790 |
Samyang Trirex® 3000H Polycarbonate, Low-temperature Impact PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3000H is a low temperature impact grade.Applications: Mobile Phone Housing, high gloss.. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP WH0420A_GY5A749 PBT 4.2 specific gravity, PBT, gray |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® V3903WX PBT+PC (Asia Pacific) Unreinforced fllame retardant PBT/PC blends with good chemical resistance and low temperature impact, UV stablized |
|||
Flexural Modulus | 1.91 GPa @Thickness 3.20 mm |
277 ksi @Thickness 0.126 in |
ASTM D790 |
Supreme Petrochem SP 6530 Antistatic Polystyrene Characteristics Prevents dust patterns due to static charges Eliminates need of coatings Fully colorable Processing Injection molding Extrusion & Forming Applications Meter housings Foodservice .. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® TP-1020 PC, Unreinforced Transparent Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | ASTM D790 |
Westlake Plastics HIPS High Impact Polystyrene, Compression Molded Compression molded HIPS is a low cost plastic material that is easily machined and fabricated. It is frequently used for preproduction prototyping. HIPS is a FDA compliant use in food processing a.. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | |
Zylog Hipolyene® 1533 NM Thermoplastic Polyolefin & PP Compound Information provided by Zylog Plastalloys Pvt. Ltd. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | |
Zylog Hipolyene® 6251 Y M2 Thermoplastic Polyolefin & PP Compound Information provided by Zylog Plastalloys Pvt. Ltd. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | |
Zylog Hipolyene® 8501 T6 B Thermoplastic Polyolefin & PP Compound Information provided by Zylog Plastalloys Pvt. Ltd. |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | ASTM D790 |
Westlake Plastics HIPS High Impact Polystyrene HIPS is a low cost plastic material that is easy to machine and fabricate. It is often specified for low strength structural applications when impact resistance, machinability, and low cost are req.. |
|||
Flexural Modulus | 1.91 GPa @Thickness 6.40 mm |
277 ksi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron SE-22M ABS Sheet Extrusion Grade Sheet Extrusion grade for profile & DoorsInformation provided by Bhansali |
|||
Flexural Modulus | 1.91 GPa @Thickness 6.40 mm |
277 ksi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron SE-32 ABS Sheet Extrusion Grade Super high and Very High Impact Sheeting grades for Automobile & Luggage ApplicationsInformation provided by Bhansali |
|||
Flexural Modulus | 1.91 GPa @Thickness 6.40 mm |
277 ksi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron SE-22M ABS Sheet Extrusion Grade Sheet Extrusion grade for profile & DoorsInformation provided by Bhansali |
|||
Flexural Modulus | 1.91 GPa @Thickness 6.40 mm |
277 ksi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron SE-32 ABS Sheet Extrusion Grade Super high and Very High Impact Sheeting grades for Automobile & Luggage ApplicationsInformation provided by Bhansali |
|||
Flexural Modulus | 1.91 GPa | 277 ksi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® WP-1041G PC/ABS, Unreinforced Metal Plating Grade Information provided by Samsung Cheil Industries. |