Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.30 GPa | 189 ksi | |
Plastcom SLOVALEN PC 16 FRD 1 PP, flame retardant Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0.. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
Premix Thermoplastics PRE-ELEC® ESD 5300 Static Dissipative Thermoplastic Compound PRE-ELEC® ESD 5300 is a static dissipative thermoplastic compound based on polypropylene homopolymer. The dissipative property is permanent and built into the polymer chain. Surface resistance valu.. |
|||
Flexural Modulus | >= 1.30 GPa | >= 189 ksi | ASTM D790 |
NIZHNEKAMSKNEFTEKHIM PP 1532B (YD50G) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
Flexural Modulus | 1.30 GPa @Temperature 100 °C |
189 ksi @Temperature 212 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded
(discontinued **) AMODEL ET-1001 L resin is an impact modified polyphthalamide (PPA) with exceptional impact strength and practical toughness. AMODEL PPA resins offer high fatigue strength, and good chemical resistan.. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | 1% Secant; ASTM D790 |
IRPC Polimaxx Polene 2300K Polypropylene Block Copolymer CHARACTERISTICS: HIGH IMPACTAPPLICATIONS: INJECTION MOLDING FOR FURNITURE, HOUSEWARES, CLOSURES, CONTAINERS, AUTOPARTS AND ELECTRICAL APPLIANCES |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | 1% Secant; ASTM D790 |
IRPC Polimaxx Polene 2300LC Polypropylene Block Copolymer CHARACTERISTICS: HIGH IMPACTAPPLICATIONS: INJECTION MOLDING FOR FURNITURES, HOUSEWARES, CLOSURES, CONTAINERS, CRATES, AUTOPARTS AND ELECTRICAL APPLIANCES |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | 1% Secant; ASTM D790 |
IRPC Polimaxx Polene 2300SC Polypropylene Block Copolymer CHARACTERISTICS: HIGH FLOW, GOOD IMPACTAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES, THIN WALL PARTS |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 A |
Metabolix Mirelâ„¢ P1004 Injection Molding Grade PHA Bioplastic Mirel P1004 is a general purpose injection molding grade with high toughness.About Mirel BioplasticsMirel is a family of bioplastic materials that have physical properties comparable to petroleum-ba.. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
LyondellBasell Hifaxâ„¢ CB228 Thermoplastic Olefin Resin Key Features: medium melt flow, medium high modulus, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, good paintability, good processabilityApplications: aut.. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
LyondellBasell Hifaxâ„¢ CB229 Thermoplastic Olefin Resin Key Features: medium high melt flow, medium high modulus, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, good dimensional stability, excellent processabili.. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | 3 points and 2 mm/min; ISO 178 |
Styron INSPIREâ„¢ TF0808S(U) Polypropylene TF0808S(U) is a talc filled PP exhibiting high impact resistance and a high stiffness. It is particularly well suited for low wall thickness bumper skins. INSPIRE TF0808S for painted parts INSPIRE .. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOTUF VX99809 Super Tough Nylon Super Tough Nylon, Proprietary Filler(s), |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
Solvay TECHNYL® A 216 PA66, Conditioned Description: Unreinforced polyamide 66, medium viscosity, for injection molding.Available in: Asia Pacific and Latin AmericaProduct Applications: TECHNYL ® A 216 offers all of the primary propert.. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
Borealis HD234CF Polypropylene HD234CF is a homopolymer film resin, suitable for the manufacturing of unoriented film on chill roll process. Applications: HD234CF is recommended for food packaging, lamination films, stationery f.. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 |
A. Schulman PP 3475-01 Polypropylene High Melt Homopolymer Polypropylene DescriptionPolypropylene PP 3475-01 Natural is a high melt homopolymer polypropylene with consistent general purpose homopolymer characteristics. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
Unipetrol PP MONSTEN® NB 218 Polypropylene Homopolymer Made for fibers applications. Basic stabilization. Homopolymer.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
Unipetrol PP MONSTEN® NB 425 Polypropylene Homopolymer Made for non-woven textiles applications. Basic stabilization. Homopolymer.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ISO 527-2 |
Total Lumicene® MR 2001 Polypropylene, Metallocene Polypropylene ATOFINA Polypropylene MR 2001 is a metallocene polypropylene, and is characterized by high fluidity for high speed spinning on spun laid non-woven lines where spun filaments are produced to form a w.. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ISO 527-2 |
Total PPH 3051 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 3051 is homopolymer.ApplicationATOFINA Polypropylene PPH 3051 is intended for the extrusion of flat bioriented films for food packaging or high strength adhesive tapes. Inf.. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 |
A. Schulman POLYFORT™ PP 3045 Information provided by A. Schulman. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 |
A. Schulman PP 3475-01 Polypropylene High Melt Homopolymer Polypropylene DescriptionPolypropylene PP 3475-01 Natural is a high melt homopolymer polypropylene with consistent general purpose homopolymer characteristics. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D 790 |
Cossa Polimeri ESTAPROP 1000 V2 K Flame Retardant Polypropylene PP copolymerFlame retardant class V2, PBDE free, good processability, good impact strengthInformation provided by Cossa Polimeri S.r.l. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | 2 mm/min; ISO 178 |
Chi Mei Polyrex® PH-55Y Polystyrene - Food Medium impact |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
ExxonMobil PP1064L1 Polypropylene Homopolymer Product Description: A homopolymer resin designed for general use. It is suitable for masterbatch carrier and other compounding applications and for the molding of caps, cups, containers and other .. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | cond; ISO 178 |
DSM EcoPaXX® Q-X07290 PA410-I Impact Modified |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | Dry; ISO 178 |
Arkema Group Orgalloy® LE 60 ES Polyamide Alloy Polyamide Alloy, Blow Molding of Technical PartsInformation provided by Arkema Group |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 |
Buckeye Polymers BP Flex D9010 UC85 TPO TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment. These resins have excellent UV resistance and have a.. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 |
A. Schulman ComAlloy Comtuf® 608 Nylon 6/12, Impact Modified Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc.. |
|||
Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
Borealis HD214CF Polypropylene Homopolymer HD214CF is a homopolymer film resin, suitable for the manufacturing of unoriented film on chill roll process. Applications: food packaging, lamination films, stationary films, multi layer co-extrus.. |
|||
Flexural Modulus | 1.30 GPa @Temperature 23.0 °C |
188 ksi @Temperature 73.4 °F |
ASTM D790A |
Ineos H03G-01 Polypropylene Homopolymer This is a homopolymer designed for tenter frame BOPP processing and meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.ApplicationsFood packagingOverwrap.. |