Polymer Property : Flexural Modulus = 0.850 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	0.850 GPa @Temperature 90.0 °C	123 ksi @Temperature 194 °F	ISO 178, ASTM D790
Nilit Nilamid A H2 FR HF2 Unfilled, Flame Retardant PA66/6 Co-Polymer Description: Nilamid A H2 FR HF2 is an unfilled, flame retardant NYLON 66/6 co-polymer that does not contain halogen or red phosphorous. This product combines excellent flow characteristics and extr..
Flexural Modulus	>= 0.850 GPa	>= 123 ksi	ASTM D790
NIZHNEKAMSKNEFTEKHIM PE 4441R (40404) Medium Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Flexural Modulus	>= 0.850 GPa	>= 123 ksi	ASTM D790
NIZHNEKAMSKNEFTEKHIM PP 4132B (PA14D) Propylene and Ethylene Copolymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates very high long-term thermal stability, thermal-oxidative degradation r..
Flexural Modulus	>= 0.850 GPa	>= 123 ksi	ASTM D790
NIZHNEKAMSKNEFTEKHIM PP 4210L (EP2C30F) Propylene and Ethylene Copolymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r..
Flexural Modulus	0.850 GPa @Temperature 23.0 °C	123 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYfill PPC 20000 Polypropylene Copolymer Information provided by Polykemi AB
Flexural Modulus	0.850 GPa @Temperature 90.0 °C	123 ksi @Temperature 194 °F	ASTM D790
LATI LATILUB 73/13-20T Polyoxymethylene Base (POM), 10% Mixed PTFE Self Lubricating Plastic (Unverified D Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri..
Flexural Modulus	0.850 GPa	123 ksi	2 mm/min; ASTM D790
Solvay Specialty Polymers Solef® 31008 PVDF Copolymer (discontinued **) Key features of this grade: High Flexibility/ High Elongation/Cold Impact Resistance, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General ..
Flexural Modulus	0.850 GPa	123 ksi	Tangent; ASTM D790
Flint Hills AP7710-HS Impact Copolymer Polypropylene TPO copolymer, UL certified, and FDA compliant.Features: Structural stiffness, ultra high impact strength, and high uniform flow rate.Applications: Injection molding: automotive items and exterior e..
Flexural Modulus	0.850 GPa @Temperature 23.0 Â°C	123 ksi @Temperature 73.4 Â°F	ISO 178
MBA Polymers PP 2182 Post-consumer recycled polypropylene copolymer Very high melt flow rate for injection molding application. Available in standard black.Information provided by MBA Polymers.
Flexural Modulus	0.850 GPa	123 ksi	1% Secant; ASTM D790
IRPC Polimaxx Polene 3325M Polypropylene Random Copolymer CHARACTERISTICS: GOOD EXTRUDABILITY, GOOD SEALABLE CONTAINS SLIP AND ANTIBLOCK ADDITIVES APPLICATIONS: CAST FILM EXTRUSION CPP FILM FOR LAMINATE , CPP FILM FOR PACKAGINGS
Flexural Modulus	0.850 GPa	123 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP FL003 PE LNP* LUBRICOMP* FL003 is a compound based on Polyethylene resin containing 15% PTFE. Added features include: Internally Lubricated.
Flexural Modulus	0.850 GPa	123 ksi	ASTM D790
Borealis Borstar® HE 6068 Natural Bimodal HDPE with very low shrinkage for Submarine and Fiber Optical Cables Borstar® HE6068 is a natural, UV-stabilized, colorable, bimodal high density (HD) jacketing compound, which is produced with the Borealis proprietary Borstar® bimodal process technology. Borstar®..
Flexural Modulus	0.850 GPa	123 ksi	ASTM D790/1
Borealis Borstar® HE6067 Black Bimodal HD Polyethylene Compound for Jacketing of Communication and Power Cables Borstar HE6067 is a black, bimodal, co-polymer high density polyethylene (HDPE) compound produced according to the bimodal Borstar process. It is characterized by its balanced properties important ..
Flexural Modulus	0.850 GPa	123 ksi	ISO 178
Borealis Daploy™ WB260HMS Polypropylene Daploy™ WB260HMS is a propylene-based, structurally isomeric polymer. Applications: cushioning and protective packaging, door liners, lightweight packaging trays, beakers and containers, microwave..
Flexural Modulus	0.850 GPa	123 ksi	at 2 in/min; ASTM D790
A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene DescriptionPolypropylene PP 1188-01 is an extra high-impact polypropylene, copolymer type, with excellent low temperature properties. Information provided by A. Schulman.
Flexural Modulus	0.850 GPa	123 ksi	at 2 in/min; ASTM D790
A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene DescriptionPolypropylene PP 1188-01 is an extra high-impact polypropylene, copolymer type, with excellent low temperature properties. Information provided by A. Schulman.
Flexural Modulus	0.850 GPa	123 ksi	at 2 in/min; ASTM D790
A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene DescriptionPolypropylene PP 1188-01 is an extra high-impact polypropylene, copolymer type, with excellent low temperature properties. Information provided by A. Schulman.
Flexural Modulus	0.850 GPa	123 ksi	at 2 in/min; ASTM D790
A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene DescriptionPolypropylene PP 1188-01 is an extra high-impact polypropylene, copolymer type, with excellent low temperature properties. Information provided by A. Schulman.
Flexural Modulus	0.850 GPa	123 ksi	DAM; ISO 178
DuPont Performance Polymers Zytel® LC6601 BK551 Nylon 612 (Unverified Data**) Plasticized Toughened Polyamide 612 Developed for Extrusion Information provided by DuPont Performance Polymers
Flexural Modulus	0.850 GPa @Temperature 23.0 °C	123 ksi @Temperature 73.4 °F	DAM; ISO 178
DuPont Performance Polymers Zytel® ST811HS BK038 Nylon 6 (Unverified Data**) Zytel® ST811HS BK038 is a flexible, non-plasticized, black Super Tough nylon 6 resin developed for extrusion and injection molding applications such as cable and rope jacketing, hose inner cores an..
Flexural Modulus	0.850 GPa	123 ksi	After conditioning at 23°C and 50% RH; ISO 178
Arkema Group Orgalloy® LE 60 SF Polyamide Alloy Polyamide Alloy, Film and PackagingInformation provided by Arkema Group
Flexural Modulus	0.850 GPa	123 ksi	1% secant; ASTM D790
Braskem CP 195 Injection Molding Polypropylene Description: CP 195 is a very high melt flow rate heterophasic copolymer developed for high speed injection moulding machines and high productivity thin-walled injection moulded parts. The product f..
Flexural Modulus	0.850 GPa	123 ksi	SAE J949
Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (3.5 mm Molded Thickness) AZDEL SuperLite® SL550900-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic..
Flexural Modulus	0.850 GPa	123 ksi	ASTM D790
Carmel Olefins CAPILENE® TR 50 Polypropylene Impact Copolymer Description: CAPILENE® TR 50 is a medium melt flow rate heterophasic copolymer with very high impact strength, even at low temperature, designed for injection molding. This grade combines good pr..
Flexural Modulus	0.850 GPa	123 ksi	ASTM D790
Carmel Olefins CAPILENE® TU 75 AV Polypropylene Impact Copolymer Description: CAPILENE® TU 75 AV is a high melt flow rate, controlled rheology heterophasic copolymer with very high impact strength, even at low temperature. It contains antistatic and nucleating..
Flexural Modulus	0.850 GPa @Temperature 93.0 °C	123 ksi @Temperature 199 °F	ASTM Test
BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Conditioned) Ultramid HPN 9362 is a 40% mineral reinforced, impact modified nylon 6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing c..
Flexural Modulus	0.850 GPa	123 ksi
Total Lacqtene® 6002 FLG 42 HDPE film (discontinued **) LACQTENE® 6002 FLG 42 is a medium density polyethylene resin with hexene as comonomer. This shows a broad molecular weight distribution ensuring outstanding processability. LACQTENE® 6002 FLG 42 h..
Flexural Modulus	0.850 GPa	123 ksi	ISO 178
Polyplastic Armlen® PP 3IM Impact Modified Polypropylene Impact modified polypropylene composite materialInformation provided by PolyPlastic Group.
Flexural Modulus	0.850 GPa	123 ksi	80x10x4 mm specimen, 2 mm/min; ISO 178
Solvay Engineered Polymers DEXPRO® R120 TPV - High-Impact Polypropylene (discontinued **) Description: DEXPRO® R120 is a reactor-grade thermoplastic elastomeric olefin resin with a good balance of impact performance, stiffness, and paintability. Applications: Painted bumper fasciasInfor..
Flexural Modulus	0.850 GPa	123 ksi	ASTM D790/1
Borealis Borstar® HE6062 HDPE Black Jacketing Compound Borstar HE6062 is a black, bimodal co-polymer high density polyethylene (HDPE) compound produced using the Borealis Borstar process. It is characterized by balanced properties important in jacketin..