Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.750 GPa | 109 ksi | 1% secant at 0.05 in/min; ASTM D790B |
LyondellBasell Montell 1900 UHMW Polyethylene Key Features: ultrahigh molecular weight polyethylene resin, excellent abrasion resistance, high impact strength, low coefficient of friction, good chemical resistance, low odor and taste transferAp.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 1% secant at 0.05 in/min; ASTM D790B |
LyondellBasell Montell 1900CM UHMW Polyethylene Key Features: ultrahigh molecular weight polyethylene resin, excellent abrasion resistance, high impact strength, low coefficient of fraction, good chemical resistance, low odor and taste transfer, .. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 1% secant at 0.05 in/min; ASTM D790B |
LyondellBasell Montell 1900H UHMW Polyethylene Key Features: ultrahigh molecular weight polyethylene resin, excellent abrasion resistance, high impact strength, low coefficient of friction, good chemical resistance, low odor and taste transfer, .. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 1% secant at 0.05 in/min; ASTM D790B |
LyondellBasell Montell 1900LCM UHMW Polyethylene Key Features: ultrahigh molecular weight polyethylene resin, excellent abrasion resistance, high impact strength, low coefficient of friction, good chemical resistance, low odor and taste transferAp.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 1% secant at 0.05 in/min; ASTM D790B |
LyondellBasell Montell HB320CM UHMW Polyethylene Key Features: ultrahigh molecular weight polyethylene resin, excellent abrasion resistance, high impact strength, low coefficient of friction, good chemical resistance, low odor and taste transfer, .. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 1.3 mm/min; ASTM D790 |
ICO Polymers ICORENEâ„¢ 155-4060 LMDPE Rotational Molding Resin Description: ICORENE 155-4060 is a linear medium density polyethylene developed for use in rotational molding. It has a great combination of stiffness and toughness in a resin that is easy processi.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 2mm/min; ASTM D790-86 |
Micropol Microcene MC122 Metallocene Based Polyethylene Rotational Molding Powder Characteristics: reduced fusion, compacting, and crystallization times or lower oven temperatures; improved wall thickness control, improved impact resistance; low warpage; better creep resistance. .. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ASTM D790 |
Micropol Microlink XL28 Crosslinkable Polyethylene Provides a finished molding of improved properties with the use of conventional rotational molding equipment. Properties include enhanced toughness (particularly low temp impact), ESCR, chemical, a.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ISO 178 |
LyondellBasell Hifaxâ„¢ CJ232 Thermoplastic Olefin Resin Key Features: medium high melt flow, medium modulus, low CLTE, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, good dimensional stability, paintableApplicat.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ISO 178-1975 |
SIDPEC EGYPTENE® HD 3840 EA MDPE Wire and Cable Grade Applications:Suitable for the production of silane cross-linkable compoundsLow voltage power cable insulationInjection molded technical parts and closureInformation provided by Interchim s.r.l., off.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ASTM D790 |
SCG Chemicals EL-Leneâ„¢ M90 Butene (C4) Rotational Molding Resin Color compound resin available in pellet / powder formKey Characteristics:High stiffness and toughnessGood ESCRFair processingTypical Applications: Large, thick-wall parts, high-load products, such.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ASTM D790 |
SCG Chemicals EL-Leneâ„¢ M9001 Butene (C4) Rotational Molding Resin Natural base resin available in pellet / powder formKey Characteristics:High stiffness and toughnessGood ESCRFair processingTypical Applications: Large, thick-wall parts, high-load products, such a.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 50% humidity; ISO 178 |
Borealis Bormed™ RB801CF Polypropylene Random Copolymer Bormed™ RB801CF is a random copolymer. Applications: Bormed™ RB801CF is intended for packaging for medical devices, pouches, and packaging for pharmaceutical products. Additives: Bormed™ RB801C.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ISO 178 |
Unipetrol PE HD LITEN® FB 10 HDPE Made for tubular film applications.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ISO 178 |
Unipetrol PE HD LITEN® RL 58 HDPE Made for injection molding and special applicationsInformation provided by Unipetrol RPA |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ISO 178 |
Unipetrol PE HD LITEN® VL 20 HDPE Extrusion and pipe applications.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 1.3 mm/min; ASTM D790 |
A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 1.3 mm/min; ASTM D790 |
A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 1.3 mm/min; ASTM D790 |
A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ISO 178 |
Borealis Borseal™ TD220BF Terpolymer for BOPP Film Borseal TD220BF is a C2/C4 terapolymer film resin especially developed for use as sealing layers in coextruded BOPP film (manufactured on stenter frame and double bubble film process).Borseal TD220B.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 0.05 in/min; ISO 178 |
CTC SunPro® SP 200 P 3085 Polypropylene Copolymer SunPro® SP 200 P 3085 is a general purpose, medium flow, polypropylene copolymer. It has applications in automotive wheel housings and general purpose automotive. Automotive Certifications: GM.PP... |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 0.05 in/min; ISO 178 |
CTC SunPro® SP 200 P 5000 Polypropylene Copolymer SunPro® SP 200 P 5000 is a general purpose, medium flow, polypropylene copolymer. It has applications in automotive wheel housings and general purpose automotive. Automotive Certifications: MS DB5.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | SAE J949 |
Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness) AZDEL SuperLite® SL550900-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ISO Data |
BASF Ultramid® 8254 HS BK-102 PA6 (Dry) Ultramid 8254 HS is a highly flexible, heat stabilized, impact modified nylon 6 extrusion grade for tubing applications. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ISO 178 |
Total Lacqtene® 2002 TN 40 HDPE, blow molding, pipe, sheet
(discontinued **) LACQTENE® 2002 TN 40 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer.Information provided provided by Total Petrochemicals.Total Petrochemic.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | |
Plastcom SLOVALEN PQ 53 N PP, imp. strength FeaturesPP modified with natural caoutchouc. The addition of thermoplastic caoutchouc causes increased toughness. General application in all industry branches. Delivered in natural mode and in the f.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | 1.3 mm/min; ASTM D790 |
A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ISO 178 |
Unipetrol PE HD LITEN® ZB 20 HDPE Made for blow molding, extrusion, and pipe applications.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 0.750 - 2.90 GPa | 109 - 420 ksi | Average value: 1.66 GPa Grade Count:46 |
Overview of materials for Acetal Copolymer, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Impact Modified". Each property range of values reported is minimum and maximum values.. |
|||
Flexural Modulus | 0.750 GPa | 109 ksi | ISO 178 |
Ascend Performance Materials Vydyne® 67R Nylon 66, Heat Stabilized, Conditioned Vydyne® 67R is a high-viscosity, heat-stabilized PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 67R resin offers high strength, .. |