Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.220 GPa | 31.9 ksi | ISO 178 |
Polimeri Europa Flexirene® MT 40 A Linear Low Density Polyethylene Flexirene MT 40 A is a linear low density polyethylene (LLDPE), with antioxidants, suitable for injection molding application.Flexirene MT 40 A is characterized by a good processability and impact r.. |
|||
Flexural Modulus | 0.220 - 9.31 GPa | 31.9 - 1350 ksi | Average value: 2.85 GPa Grade Count:307 |
Overview of materials for PVC, Rigid Grade This property data is a summary of similar materials in the MatWeb database for the category "PVC, Rigid Grade". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Flexural Modulus | 0.220 GPa | 31.9 ksi | ASTM D790 |
DuPont™ Surlyn® 8527 Ionomer Resin, Sodium
(discontinued **) Surlyn® 8527 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu.. |
|||
Flexural Modulus | 0.220 GPa | 31.9 ksi | ISO 178 |
Metabolix M-vera™ B5010 Film Grade Compostable Bioplastic For use in tough, certified compostable film and bag applications. Mvera B5010 offers a wide range of attractive traits—excellent tear and puncture toughness, excellent seal strength, good prin.. |
|||
Flexural Modulus | 0.220 GPa | 31.9 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP YL003 Polyester Elastomer LNP* LUBRICOMP* YL003 is a compoudn based on Polyester Elastomer resin containing 15% PTFE. Added feature of this grade is: Wear Resistant. |
|||
Flexural Modulus | 0.220 GPa | 31.9 ksi | ASTM D790 |
Covestro Baydur® 646 Polyurethane Structural Foam RIM, Density 15 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Flexural Modulus | 0.220 GPa | 31.9 ksi | ASTM D790 |
DuPont™ HPF® 1000 Amorphous Polymer for Golf Balls DuPont™ HPF 1000 is extremely versatile and can be used to manufacture all layers of golf balls. DuPont™ HPF 1000 offers a combination of high resilience and low compression. This polymer is a hig.. |
|||
Flexural Modulus | 0.220 GPa | 31.9 ksi | ASTM D790 |
DuPont™ Surlyn® 9650 Ionomer Resin, Zinc Surlyn® 9650 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
Flexural Modulus | 0.220 GPa | 31.9 ksi | SAE J949 |
Azdel SuperLite® SL552000-100 PP Resin Matrix / 55% Glass Fiber (10 mm Molded Thickness) AZDEL SuperLite® SL552000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Modulus | 0.220 GPa @Temperature 93.0 °C |
31.9 ksi @Temperature 199 °F |
ASTM Test |
BASF Ultramid® HPN 9350 HS PA6 (Dry) Ultramid HPN 9350 HS is a flexible, heat stabilized, impact modified PA6 extrusion grade resin. It possesses a balance of performance properties such as good flexibility, toughness and abrasion res.. |
|||
Flexural Modulus | 0.220 GPa | 31.9 ksi | ISO 178 |
Teknor Apex Sinvicomp DFR 5806 Polyvinyl Chloride, Rigid Availability: Asia Pacific Features: Good Impact Resistance Uses: Profiles Forms: Powder Processing Method: ExtrusionInformation Provided by Teknor Apex |