Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 45.0 MPa @Temperature 982 °C, Time 3.60e+6 sec |
6530 psi @Temperature 1800 °F, Time 1000 hour |
2 mm sheet |
Haynes NS-163® Cobalt Alloy Alloy that brings high-temperature alloy performance at temperatures up to 2200°F (1204°C). HAYNES NS-163 alloy is a wrought cobalt-based alloy (Co–28Cr–21Fe–9Ni–1.25Tiâ€.. |
|||
Rupture Strength | 45.0 MPa @Temperature 925 °C, Time 36000 sec |
6530 psi @Temperature 1700 °F, Time 10.0 hour |
Initial Stress |
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750) Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600°F (870°C). It is widely used as a wrought material for.. |
|||
Rupture Strength | 45.0 MPa @Temperature 800 °C, Time 3.60e+7 sec |
6530 psi @Temperature 1470 °F, Time 10000 hour |
Stress Rupture |
AFE Technologies Cronite 37Ni/18Cr/Nb No. HR32 High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF.. |