Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 20.0 MPa @Temperature 850 °C, Time 3.60e+7 sec |
2900 psi @Temperature 1560 °F, Time 10000 hour |
|
Outokumpu 353MA® High Temperature Austenitic Stainless Steel Alloy with higher nickel content than the other steels. Has increased silicon and nitrogen contents and is microalloyed with rare earth metals (REM). Max service temperature in air is 1150°C, but.. |
|||
Rupture Strength | 20.0 MPa @Temperature 800 °C, Time 3.60e+7 sec |
2900 psi @Temperature 1470 °F, Time 10000 hour |
|
Outokumpu 4841 High Temperature Austenitic Stainless Steel Variant of 1.4845 with an increased silicon content which enhances the steel's resistance to oxidation/corrosion but has also made it more susceptible to embrittlement.Applications: Heat and creep r.. |
|||
Rupture Strength | 20.0 MPa @Temperature 899 °C, Time 3.60e+7 sec |
2900 psi @Temperature 1650 °F, Time 10000 hour |
|
ATI Allegheny Ludlum 310 Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Rupture Strength | 20.0 MPa @Temperature 899 °C, Time 3.60e+7 sec |
2900 psi @Temperature 1650 °F, Time 10000 hour |
|
ATI Allegheny Ludlum 310H Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Rupture Strength | 20.0 MPa @Temperature 899 °C, Time 3.60e+7 sec |
2900 psi @Temperature 1650 °F, Time 10000 hour |
|
ATI Allegheny Ludlum 310S Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Rupture Strength | 20.0 MPa @Temperature 899 °C, Time 3.60e+7 sec |
2900 psi @Temperature 1650 °F, Time 10000 hour |
|
ATI Allegheny Ludlum 310Si Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Rupture Strength | 20.0 MPa @Temperature 950 °C, Time 3.60e+7 sec |
2900 psi @Temperature 1740 °F, Time 10000 hour |
Stress Rupture |
AFE Technologies Cronite Standard Nickel Alloy Castings, No. HR4 High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF.. |