Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 83.0 MPa @Temperature 871 °C, Time 3.60e+6 sec |
12000 psi @Temperature 1600 °F, Time 1000 hour |
|
Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Rupture Strength | 83.0 MPa @Temperature 927 °C, Time 360000 sec |
12000 psi @Temperature 1700 °F, Time 100 hour |
|
Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Rupture Strength | 83.0 MPa @Temperature 650 °C, Time 3.60e+6 sec |
12000 psi @Temperature 1200 °F, Time 1000 hour |
Typical Stress-Rupture |
Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C) Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200°F (650°C). It is principally used in low stress elevated temperature applications requiring reas.. |
|||
Rupture Strength | 83.0 MPa @Temperature 677 °C, Time 3.60e+7 sec |
12000 psi @Temperature 1250 °F, Time 10000 hour |
|
ATI Allegheny Ludlum 309 Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Rupture Strength | 83.0 MPa @Temperature 677 °C, Time 3.60e+7 sec |
12000 psi @Temperature 1250 °F, Time 10000 hour |
|
ATI Allegheny Ludlum 309H Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Rupture Strength | 83.0 MPa @Temperature 677 °C, Time 3.60e+7 sec |
12000 psi @Temperature 1250 °F, Time 10000 hour |
|
ATI Allegheny Ludlum 309S Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Rupture Strength | 83.0 MPa @Temperature 677 °C, Time 3.60e+7 sec |
12000 psi @Temperature 1250 °F, Time 10000 hour |
|
ATI Allegheny Ludlum 309Si Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Rupture Strength | 83.0 MPa @Temperature 927 °C, Time 360000 sec |
12000 psi @Temperature 1700 °F, Time 100 hour |
|
Haynes 282® Nickel Alloy Sheet, Gamma-Prime Strengthened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |
|||
Rupture Strength | 83.0 MPa @Temperature 871 °C, Time 3.60e+6 sec |
12000 psi @Temperature 1600 °F, Time 1000 hour |
|
Haynes 282® Nickel Alloy Sheet, Gamma-Prime Strengthened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |