Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 8.30 MPa @Temperature 870 °C, Time 3.60e+6 sec |
1200 psi @Temperature 1600 °F, Time 1000 hour |
Typical Stress-Rupture |
Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C) Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200°F (650°C). It is principally used in low stress elevated temperature applications requiring reas.. |
|||
Rupture Strength | 8.27 MPa @Temperature 982 °C, Time 3.60e+7 sec |
1200 psi @Temperature 1800 °F, Time 10000 hour |
|
Carlson C 800H Nickel-Iron-Chromium Alloy General DescriptionCarlson Alloy C 800 is a nickel-iron-chromium alloy, combining high strength with excellent resistance to oxidation and carburization at elevated temperatures. This alloy resists.. |