Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 70.0 MPa @Temperature 650 °C, Time 3.60e+7 sec |
10200 psi @Temperature 1200 °F, Time 10000 hour |
|
Outokumpu 4828 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
Rupture Strength | 70.0 MPa @Temperature 650 °C, Time 3.60e+7 sec |
10200 psi @Temperature 1200 °F, Time 10000 hour |
|
Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
Rupture Strength | 70.0 MPa @Temperature 705 °C, Time 360000 sec |
10200 psi @Temperature 1300 °F, Time 100 hour |
Typical Stress-Rupture |
Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C) Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200°F (650°C). It is principally used in low stress elevated temperature applications requiring reas.. |
|||
Rupture Strength | 70.0 MPa @Temperature 750 °C, Time 3.60e+7 sec |
10200 psi @Temperature 1380 °F, Time 10000 hour |
Stress Rupture |
AFE Technologies Cronite Standard Nickel Alloy Castings, No. HR4 High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF.. |