Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 28.0 MPa @Temperature 800 °C, Time 3.60e+7 sec |
4060 psi @Temperature 1470 °F, Time 10000 hour |
|
Outokumpu 353MA® High Temperature Austenitic Stainless Steel Alloy with higher nickel content than the other steels. Has increased silicon and nitrogen contents and is microalloyed with rare earth metals (REM). Max service temperature in air is 1150°C, but.. |
|||
Rupture Strength | 28.0 MPa @Temperature 750 °C, Time 3.60e+7 sec |
4060 psi @Temperature 1380 °F, Time 10000 hour |
|
Outokumpu 4841 High Temperature Austenitic Stainless Steel Variant of 1.4845 with an increased silicon content which enhances the steel's resistance to oxidation/corrosion but has also made it more susceptible to embrittlement.Applications: Heat and creep r.. |
|||
Rupture Strength | 28.0 MPa @Temperature 900 °C, Time 3.60e+7 sec |
4060 psi @Temperature 1650 °F, Time 10000 hour |
Stress Rupture |
AFE Technologies Cronite Standard Nickel Alloy Castings, No. HR4 High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF.. |
|||
Rupture Strength | 28.0 MPa @Temperature 1040 °C, Time 360000 sec |
4060 psi @Temperature 1900 °F, Time 100 hour |
|
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed.. |
|||
Rupture Strength | 28.0 MPa @Temperature 980 °C, Time 3.60e+6 sec |
4060 psi @Temperature 1800 °F, Time 1000 hour |
|
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed.. |