Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 200 MPa @Temperature 705 °C, Time 3.60e+6 sec |
29000 psi @Temperature 1300 °F, Time 1000 hour |
Initial Stress |
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750) Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600°F (870°C). It is widely used as a wrought material for.. |
|||
Rupture Strength | 200 MPa @Temperature 816 °C, Time 3.60e+6 sec |
29000 psi @Temperature 1500 °F, Time 1000 hour |
|
Special Metals UDIMET® alloy R41 Ni-Cr Alloy UDIMET® alloy R41 (UNS N07041) is a precipitation-hardenable nickel-chromium alloy containing significant amounts of cobalt and molybdenum, along with lesser amounts of aluminum and titanium. Al.. |
|||
Rupture Strength | 200 MPa @Temperature 760 °C, Time 360000 sec |
29000 psi @Temperature 1400 °F, Time 100 hour |
|
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed.. |