Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 120 MPa @Temperature 600 °C, Time 3.60e+7 sec |
17400 psi @Temperature 1110 °F, Time 10000 hour |
|
Outokumpu 4828 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
Rupture Strength | 120 MPa @Temperature 600 °C, Time 3.60e+7 sec |
17400 psi @Temperature 1110 °F, Time 10000 hour |
|
Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
Rupture Strength | 120 MPa @Temperature 816 °C, Time 3.60e+6 sec |
17400 psi @Temperature 1500 °F, Time 1000 hour |
|
Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°.. |