Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 110 MPa @Temperature 705 °C, Time 36000 sec |
16000 psi @Temperature 1300 °F, Time 10.0 hour |
Typical Stress-Rupture |
Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C) Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200°F (650°C). It is principally used in low stress elevated temperature applications requiring reas.. |
|||
Rupture Strength | 110 MPa @Temperature 816 °C, Time 3.60e+6 sec |
16000 psi @Temperature 1500 °F, Time 1000 hour |
Sheet |
Special Metals UDIMET® alloy 188 Cobalt-base Alloy UDIMET® alloy 188 (UNS R30188) is a cobalt-base alloy with excellent high-temperature strength and good oxidation resistance to 2000°F (1093°C). The high chromium level coupled with small .. |