Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Creep Modulus, 1000 hours | 700 - 1800 MPa | 102000 - 261000 psi | Average value: 1260 MPa Grade Count:20 |
Overview of materials for Polybutylene Terephthalate (PBT), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Unreinforced, Molded". Each property range of values reported is minim.. |
|||
Tensile Creep Modulus, 1000 hours | 700 - 1600 MPa | 102000 - 232000 psi | Average value: 1280 MPa Grade Count:9 |
Overview of materials for Polybutylene Terephthalate (PBT), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Extrusion Grade". Each property range of values reported is minimum an.. |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | Average value: 700 MPa Grade Count:3 |
Overview of materials for Nylon 66, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum .. |
|||
Tensile Creep Modulus, 1000 hours | 700 - 8300 MPa | 102000 - 1.20e+6 psi | Average value: 3230 MPa Grade Count:3 |
Overview of materials for Nylon, Amorphous Transparent Alloy This property data is a summary of similar materials in the MatWeb database for the category "Nylon, Amorphous Transparent Alloy". Each property range of values reported is minimum and maximum value.. |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | ISO 899-1 |
Lanxess Durethan® A 30 H2.0 901510 Nylon 66 PA 66 standard injection molding grade, non-reinforced, very easy release, good heat-ageing resistanceApplication Examples: terminal blocks, cable clips, bobbins, gearwheels |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | ISO 899-1 |
Lanxess Durethan® B 31 SK 000000 Nylon 6 PA 6, injection molding grade, non-reinforced, easy flow, easy-release, rapid solidification, crystallizes somewhat more finely and uniformly than B 30 S |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | ISO 899-1 |
Lanxess Pocan® S 1506 000000 PBT PBT, non-reinforced, injection molding extrusion, impact modified |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | ISO 899-1 |
Lanxess Durethan® A 30 000000 Nylon 66 PA 66, standard injection molding grade, non-reinforced, very easy release, normal solidificationApplication Examples: terminal blocks, cable clips, bobbins, gearwheels |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa @Temperature 23.0 °C |
102000 psi @Temperature 73.4 °F |
50%RH; ISO 899 |
DuPont Performance Polymers Zytel® ST801A NC010A Nylon 66
(Unverified Data**) Zytel® ST801A NC010A is a Super Tough, high performance, polyamide 66 resin. It is partially UV stabilized and when appropriately colored offers limited protection to indirect sunlight exposure.Inf.. |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | ISO 899 |
BASF Ultramid® A34 01 PA66 (Conditioned) Ultramid A34 01 is an intermediate visosity, PA66 grade. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German BfR recommendation "X Polyamide", 1.6.1998 or .. |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | ISO 899 |
BASF Ultramid® B3K PA6 (Conditioned) Ultramid B 3K is an easy flowing, stabilized for fast processing, grade of nylon 6. |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | ISO 899-1 |
BASF Ultraform® N2650 Z2 (LEV) POM Description: Is a POM + PUR, elastomer-modified injection-molding grades with high impact strength for clips, snap and fastening elements, also for components subject to impact stress.Information pr.. |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | ISO 899-1 |
BASF Ultramid® A3K BK 00464 PA66 (Conditioned) Description: Easy flowing injection-molding grade for fast processing. Uses include highly stressed technical parts such as bearings and gear wheels; also electrically insulating parts such as termi.. |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa @Strain <=0.500 % |
102000 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultramid® A4H PA66 (Dry) Description: Highly heat aging resistant, medium-viscosity injection-molding grade for highly stressed parts such as bearing cages, gearwheels, spool bodies and chain drive tensioners.Information pr.. |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa @Strain <=0.500 % |
102000 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultramid® B3K BK00464 PA6 (Conditioned) Description: Easy flowing and stabilized injection-molding grade used for technical parts with wall thicknesses >2 mm, e.g. machinery components, fans and power tool housings.Information provided by.. |
|||
Tensile Creep Modulus, 1000 hours | 700 MPa @Time 3.60e+6 sec |
102000 psi @Time 1000 hour |
50%RH; ISO 899-1 |
DuPont Performance Polymers Zytel® 101 NC010 Nylon 66
(Unverified Data**) Unreinforced Polyamide 66Zytel 101 NC010 is a general purpose polyamide 66 resin for injection molding and extrusion.Information provided by DuPont Performance Polymers |