Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | Temperature at which a 2 mm film achieves a seal strength of 4.4N/13mm. Tested at 0.5s dwell, 0.27 N/mm² bar pressure, 305mm/min. pull speed.; NOVA Chemicals test method |
NOVA Chemicals Sclair® FPr017-D Octene LLDPE Film Resin FPr017-D complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food. FPr0.. |
|||
Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | Temperature at which a 2-mil film achieves a seal strength of 4.4N/13mm. Tested at 0.5s dwell, 0.27 N/mm² bar pressure, 305mm/min. pull speed. |
NOVA Chemicals Surpass® FPs117-C Octene Copolymer sLLDPE Film Resins FPs117-C complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food, without .. |
|||
Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | 2N |
NOVA Chemicals Surpass® HPs900-C Octene sLLDPE Film Resin Features: Easy processabilityExceptional clarity and glossLow gelExcellent seal properties Applications: High clarity applications Lamination film Coextruded sealant layerHigh toughness filmInformat.. |
|||
Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | Temperature at which a 2-mil film achieves a seal strength of 4.4N/13mm. Tested at 0.5s dwell, 0.27 N/mm² bar pressure, 305mm/min. pull speed. |
NOVA Chemicals Surpass® FPs016-C Octene sLLDPE Film Resin FPs016-C complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food.NOVA Chem.. |
|||
Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | 2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
Dow FLEXOMER™ ETS-9064 NT 7, 2mil Very Low Density Polyethylene (VLDPE) Resin FLEXOMER™ ETS-9064 NT 7 is intended for use in single of multi-layer blown-film constructions or thick sheets. Films extruded from ETS-9064 NT 7 have a high tear strength, high impact strength, an.. |
|||
Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | Sealing Initial Temperature; Braskem® Method |
Braskem BC 818 LDPE Extrusion Coating Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Extrusion coating. Information provided by Braskem |
|||
Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | 2N |
NOVA Chemicals Surpass® FPs117-D Octene sLLDPE Film Resin
(discontinued **) Applications: Lamination Film, coextruded sealant layer, high toughness filmInformation provided by Nova Chemicals |
|||
Heat Seal Strength Initiation Temperature | <= 100 °C | <= 212 °F | Heat Seal Threshold; 0.4 N/cm; Coating on BOPP |
Solvay Specialty Polymers Diofan® A 036 Polyvinylidene Chloride (PVDC)
(discontinued **) DIOFAN® A 036 is a PVDC latex used as a flexible under layer for coating on paper and cardboard, to be covered with an appropriate topcoat.Additional Information: PROCESSING - DRYING - DIOFAN® A 0.. |
|||
Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | Average value: 100 °C Grade Count:3 |
Overview of materials for Linear Low Density Polyethylene (LLDPE)/Octene, Film This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE)/Octene, Film". Each property range of values reported is minimum.. |
|||
Heat Seal Strength Initiation Temperature | 100 - 105 °C | 212 - 221 °F | Average value: 104 °C Grade Count:8 |
Overview of materials for Low Density Polyethylene (LDPE), Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Film Grade". Each property range of values reported is minimum and maxi.. |