Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 50.0 - 90.0 MPa | 7250 - 13100 psi | Average value: 76.8 MPa Grade Count:26 |
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Shear Strength | 72.0 - 90.0 MPa | 10400 - 13100 psi | Average value: 81.0 MPa Grade Count:8 |
Overview of materials for Nylon 66, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. .. |
|||
Shear Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | IS 867-1963 |
Amity Thermosets ATS 135 Phenolic Molding Inorganic and glass fiber Filler, Compression Molded Characteristics: Self lubricating Good mechanical strength Low co-efficient of friction Good thermal conductivity Heat stable (200°C) Good mouldability Not suitable for electrical application Color.. |
|||
Shear Strength | 75.0 - 90.0 MPa | 10900 - 13100 psi | 2mm/min.; IS 867-1963 |
Amity Thermosets AMP 481 Phenolic Molding Organic and inorganic Filler, Compression Molded Characteristics:Good tracking resistanceGood dielectric strengthGood electrical insulation
Applications:Switchgear components which ought to have high tracking resistanceCircuit protecting switche.. |
|||
Shear Strength | 70.0 - 90.0 MPa | 10200 - 13100 psi | 2mm/min.; IS 867-1963 |
Amity Thermosets ATO 1510 Phenolic Molding Glass fiber Filler, Compression Molded Characteristics:Shock resistantElectrical low lossHigh mechanical strengthHeat stableHigh electrical insulationDimensional stabilityGood mechanical tension bearing strengthMedium copper adhesionColo.. |