Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 3.31 MPa | 480 psi | Plate Shear, L Direction, typ |
Hexcel® HexWeb® HRH-10 - 1/8- 8.0 Aramid Fiber/Phenolic Resin Honeycomb Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the h.. |
|||
Shear Strength | >= 3.31 MPa | >= 480 psi | Plate Shear, L Direction, min, preliminary value obtained at .500 inch thickness |
Hexcel® HexWeb® HRH-327 - 3/8 - 7.0 Fiberglass Reinforced Polyimide Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb® HRH-327 is a glass-fabric, bias weave reinforced plastic honeycomb that incorporates a polyimide resin system for the node adhesive as well a.. |
|||
Shear Strength | 3.31 MPa | 480 psi | Plate Shear, W Direction, typ |
Hexcel® HexWeb® CR III 3/16-5052-.003 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
Shear Strength | >= 3.31 MPa | >= 480 psi | Plate Shear, L Direction, min |
Hexcel® HexWeb® CR III 3/16-5056-.002 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
Shear Strength | 3.31 MPa | 480 psi | Plate Shear, W Direction, typ |
Hexcel® HexWeb® CR-PAA™ 3/16-5052-0.003 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa.. |
|||
Shear Strength | >= 3.31 MPa | >= 480 psi | Plate Shear, L Direction, min |
Hexcel® HexWeb® CR-PAA™ 3/16-5056-0.002 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa.. |
|||
Shear Strength | 3.31 MPa | 480 psi | Overlap, Acrylic/Acrylic |
3M Scotch-Weld™ DP110 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 3.31 MPa | 480 psi | Overlap, Polystyrene (HIPS) (IPA/abrade/IPA), Adhesive Failure/Substrate Failure; ASTM D1002 |
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i.. |
|||
Shear Strength | 3.31 MPa @Temperature 121 °C |
480 psi @Temperature 250 °F |
Solvent Wiped Cold Rolled Steel Overlap |
3M Scotch-Weld™ EC-2086 Structural Adhesive 3M™ Scotch-Weld™ Structural Adhesive EC-2086 is a one-part, 100% solids thermosetting liquid adhesives.Information provided by 3M |
|||
Shear Strength | 3.31 MPa | 480 psi | On Douglas Fir |
3M Scotch-Weld™ 3762LM Low Melt Adhesive Excellent “hot-tack”, fast setting for corrugated, beadboard, recouperage, repacking chipboard, wood; Economical, general purpose and Use with low melt applicator onlyInformation provided by 3M |
|||
Shear Strength | 3.31 MPa | 480 psi | Overlap, Polycarbonate-IPA/abrade/IPA, Adhesive Failure |
3M Scotch-Weld™ LSB60 Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60 is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of f.. |