Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 31.0 MPa | 4500 psi | Die |
Parker Chomerics CHO-BOND SV713 Conductive Epoxy CHO-BOND® 700 Series Adhesives for Microelectronics Packaging; these pure silver-filled epoxy pastes are designed to meet the demanding requirements of semiconductor and microelectronic packaging. .. |
|||
Shear Strength | 31.0 MPa | 4500 psi | |
Resinlab® RC8038 Anaerobic Retaining Compound The RC 8000 Series anaerobic retaining compounds are designed for use in demanding applications to fill the spaces and surface irregularities between tightly mated cylindrical parts. These products .. |
|||
Shear Strength | 31.0 MPa | 4500 psi | Interlaminar shear. |
Type P-VSB-32 (Union Carbide) Carbon Fiber Pitch fibers are prepared by heating aromatic compounds above 350°C. A dehydrogenation condensation reaction occurs to form planar aromatic molecules which aggregate into a liquid crystalline phas.. |
|||
Shear Strength | 31.0 MPa | 4500 psi | ASTM D732 |
KYDEX® 100 Acrylic/PVC Thermoplastic Sheet High impact fire rated sheetApplications: Housings for equipment such as photocopy machines, instrument panels, computers, keyboards, telephones. Hidden parts for equipment such as vending machines.. |
|||
Shear Strength | 31.0 MPa @Temperature 21.1 °C |
4500 psi @Temperature 70.0 °F |
Lap Shear |
Hexcel® Redux® 609U Adhesive film for bonding metallic and composite components Redux 609 is a 250°F curing modified epoxy film adhesive containing a cottom scrim for easy handling and glue-line thickness control. It is available at standard areal weights of 0.06 psf and 0.04 .. |
|||
Shear Strength | 31.0 MPa @Temperature 150 °C |
4500 psi @Temperature 302 °F |
90º, ILSS Short Beam, Wet; EN2563 |
Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 52%/G1177 Glass/Carbon Fiber Information provided by HexCel |
|||
Shear Strength | 31.0 MPa | 4500 psi | Short Beam Shear; ASTM D2344 |
Bedford Plastics Glass Reinforced FR Polyester Structural Fiberglass Profiles Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod.. |
|||
Shear Strength | 31.0 MPa | 4500 psi | Short Beam Shear; ASTM D2344 |
Bedford Plastics Glass Reinforced Polyester Structural Fiberglass Profiles Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded products feature:High StrengthCorrosion Resistant to many che.. |
|||
Shear Strength | 31.0 MPa | 4500 psi | Short Beam Shear; ASTM D2344 |
Bedford Plastics Glass Reinforced Vinylester Structural Fiberglass Profiles Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod.. |
|||
Shear Strength | 31.0 MPa | 4500 psi | Overlap, Aluminum Etched |
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 31.0 MPa @Temperature 23.0 °C |
4500 psi @Temperature 73.4 °F |
Aluminum Overlap |
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 31.0 MPa @Temperature -55.0 °C |
4500 psi @Temperature -67.0 °F |
Aluminum Overlap |
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 31.0 MPa | 4500 psi | Overlap, Aluminum Etched |
3M Scotch-Weld™ DP460 NS Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 31.0 MPa | 4500 psi | Overlap, Aluminum Etched |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 31.0 MPa @Temperature 23.0 °C |
4500 psi @Temperature 73.4 °F |
Aluminum, Overlap |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 31.0 MPa @Temperature -55.0 °C |
4500 psi @Temperature -67.0 °F |
Aluminum, Overlap |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 31.0 MPa | 4500 psi | Overlap, Etched Aluminum, RT, DI Water 30 days immersion, Cohesive Failure |
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i.. |
|||
Shear Strength | 31.0 MPa | 4500 psi | Overlap, Etched Aluminum, 10W30 Motor Oil at RT for 30 days immersion, Cohesive Failure |
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i.. |
|||
Shear Strength | 31.0 MPa | 4500 psi | Overlap, Etched Aluminum, -40°C/38°C and 100% RH/90°C; for 30 days, Cohesive Failure |
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i.. |
|||
Shear Strength | 31.0 MPa | 4500 psi | Aluminum, etched, Overlap, 30 day 65°C/80% RH, Cohesive Failure |
3M Scotch-Weld™ LSB60 Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60 is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of f.. |
|||
Shear Strength | 31.0 MPa @Temperature 23.0 °C |
4500 psi @Temperature 73.4 °F |
Aluminum, etched, Overlap, Cohesive Failure |
3M Scotch-Weld™ LSB60 Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60 is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of f.. |
|||
Shear Strength | 31.0 MPa @Temperature 23.0 °C |
4500 psi @Temperature 73.4 °F |
Aluminum, etched, Overlap, Cohesive Failure |
3M Scotch-Weld™ LSB60NS Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60NS is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of.. |
|||
Shear Strength | 31.0 MPa | 4500 psi | Overlap, Aluminum Etched |
3M Scotch-Weld™ DP420 Black Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 31.0 MPa | 4500 psi | Overlap, Isopropyl Alcohol immersion, RT for 30 days |
3M Scotch-Weld™ DP420 Black Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 31.0 MPa @Temperature -55.0 °C |
4500 psi @Temperature -67.0 °F |
Aluminum Overlap |
3M Scotch-Weld™ DP420 Black Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 31.0 MPa @Temperature 23.0 °C |
4500 psi @Temperature 73.4 °F |
Aluminum Overlap |
3M Scotch-Weld™ DP420 Black Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 31.0 - 96.5 MPa | 4500 - 14000 psi | Average value: 49.4 MPa Grade Count:5 |
Overview of materials for Vinyl Ester Sheet Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Vinyl Ester Sheet Molding Compound". Each property range of values reported is minimum and maximum value.. |