Polymer Property : Shear Strength = 12000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	82.7 MPa @Temperature 22.8 °C	12000 psi @Temperature 73.0 °F	ASTM D732
Quadrant EPP KETRON® MD PEEK, A Metal-Detectable Polyetheretherketone
Shear Strength	83 MPa	12000 psi	ASTM D732
Quadrant EPP Semitron® MDS 100 (ASTM Product Data Sheet)
Shear Strength	83 MPa	12000 psi	ASTM D732
Quadrant EPP Semitron® MPR-1000 (ASTM Product Data Sheet)
Shear Strength	82.7 MPa	12000 psi	Short Beam Shear, 0° Direction, RT, Dry; ASTM D2344
Renegade Materials Corporation RM-5003 Cyanate Ester Prepreg 4581 Quartz Fabric Low dielectric and loss, high performance prepreg. 350°F Cure Developed with consistent handling and superior performance Designed for demanding electrical, radome and antennae applications Del..
Shear Strength	82.7 MPa	12000 psi
Chevron Phillips Ryton® A-200 PPS Polyphenylene Sulfide (discontinued **) Ryton® PPS is used in many electronic and automotive applications because of its high strength, favorable electrical properties, and high temperature stability.Data provided by the manufacturer.Sol..
Shear Strength	83.0 MPa	12000 psi	ASTM D732
Solvay Specialty Polymers Amodel® FR-4133 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry as Molded (d AMODEL FR-4133 is a 33% glass-reinforced polyphthalamide (PPA) resin designed for electrical and electronic applications. This UL94-V0 resin offers the highest mechanical and electrical properties, ..
Shear Strength	82.6 MPa	12000 psi	ASTM D732
Solvay Specialty Polymers AvaSpire® AV-651 GF30 Polyaryletherketone (PAEK) (Unverified Data**) AvaSpire AV-651 GF30 is a 30% glass fiber reinforced polyaryletherketone (PAEK) that has been specifically formulated to provide higher mechanical strength and stiffness than unfilled AV-651 resin. ..
Shear Strength	82.7 MPa	12000 psi
XXX Phenolic Laminate Paper based phenolic provides low cost electrical and mechanical properties. It is widely used for switchboards, panel boards, insulating washers, and intricate punched parts.Information provided b..
Shear Strength	82.7 MPa @Thickness 15.7 mm	12000 psi @Thickness 0.620 in	ASTM D732
Industrial Laminates/Norplex NP320U Cotton Fabric Description: Utility version of NP320E. Meets most, but not all, NEMA properties for L and LE, and is not certifiable as a NEMA Grade.Thickness Tested: 0.062", 0.125", and 0.500"
Shear Strength	82.7 MPa @Thickness 15.7 mm	12000 psi @Thickness 0.620 in	ASTM D732
Industrial Laminates/Norplex NP691 Paper Base Laminate Description: Flame resistant, room temperature punching grade. NP691 is very similar to NP612 in electrical properties and mechanical strength, with improved moisture resistance.Thickness Tested: 0...
Shear Strength	83.0 MPa	12000 psi	ASTM D732
Glastic Laminates/Shapes 1580 Polyester Laminate Data provided by Glastic Corporation.NEMA GPO-3. Developed to meet the television industry's safety assurance requirements.
Shear Strength	82.7 MPa @Thickness 15.7 mm	12000 psi @Thickness 0.620 in	ASTM D732
Industrial Laminates/Norplex NP318 Cotton Fabric Description: Post-forming canvas phenolic material. Mechanical and electrical properties similar to NP310E. It is made from a cotton fabric weighing more than 4 ounces per square yard and having a t..
Shear Strength	82.7 - 96.5 MPa	12000 - 14000 psi
SGL Carbon Group SIGRAFIL CÂ® in 250Â°F Epoxy 60% fiber volumeInformation provided by SGL Carbon Group
Shear Strength	82.6 MPa	12000 psi	ASTM D732
Solvay Specialty Polymers AvaSpireÂ® AV-651 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber AvaSpireÂ® AV-651 GF30 is a 30% glass fiber reinforced polyaryletherketone (PAEK) that has been specifically formulated to provide higher mechanical strength and stiffness than unfilled AV-651 res..
Shear Strength	82.7 MPa	12000 psi	ASTM D732
Techmer ES ElectrafilÂ® J-1/CF/20 Nylon 66, 20% Carbon Fiber Reinforced
Shear Strength	82.7 MPa	12000 psi	Short Beam; ASTM D2344
Zyvex Performance Materials Arovex™ 250 Carbon Nanotube Strengthened Prepreg Arovex® 250 Prepreg is a 180°F (82°C) to 280°F (138°C) curing carbon nanotube strengthened epoxy prepreg suitable for numerous composites applications. Normal curing takes place at 250°F (121°..
Shear Strength	83.0 MPa	12000 psi	0º, ILSS (Short Beam), RT, Dry; EN2563
Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, 37%/7781 Fiber Information provided by HexCel
Shear Strength	82.7 MPa	12000 psi	ASTM D3846
CIP Composites 100 Series Laminated Polymer Bearing Material The 100 series consists of polyester fabric and one of several solid lubricants (optional) in a resin matrix. Non-metallic, high load, high impact and self lubricating laminated material. Laminated..
Shear Strength	83.0 MPa @Temperature 23.0 °C	12000 psi @Temperature 73.4 °F	DAM; ASTM D732
DuPont Performance Polymers Zytel® 77G43L NC010 Nylon 612 (Unverified Data**) Zytel® 77G43L NC010 is a 43% glass fiber reinforced polyamide 612 resin for injection molding.Information provided by DuPont Performance Polymers
Shear Strength	82.7 MPa @Thickness 15.7 mm	12000 psi @Thickness 0.620 in	ASTM D732
Industrial Laminates/Norplex NP321 Cotton Fabric (discontinued **) Description: NP321 consists of a fine weave cotton fabric (linen) impregnated with a phenolic resin binder. Applications include vanes for air and liquid pumps, and compressors. NP321 remains very f..