Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 10.3 - 17.2 MPa | 1500 - 2500 psi | |
ND Industries 533 Retaining Compound High strength sealing applications for non migration material |
|||
Shear Strength | 10.3 MPa | 1500 psi | Cured 6 minutes at 130°C, Al/Al |
Resin Technology Group TIGA 905 One-Part Silver Conductive Epoxy System Cure 6 minutes at 130°C or 3 minutes at 150°C.TIGA 905 is a stress-absorbing and electrically conductive, silver-filled epoxy adhesive recommended for solder replacement in microelectronic interco.. |
|||
Shear Strength | >= 10.3 MPa | >= 1500 psi | Cured 10 minutes at 120°C, Al/Al (etched) |
Resin Technology Group TIGA 951 One-Part Silver Conductive Epoxy System Cure 10 minutes at 120°CTIGA 951 is an electrically conductive, silver-filled epoxy adhesive recommended for electronic bonding and sealing applications. This one-part, smooth paste formulation of .. |
|||
Shear Strength | 10.3 - 13.8 MPa | 1500 - 2000 psi | |
ITW Plexus Plexusâ„¢ MA320 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Excellent low temperature and toughness properties.Information provided by Illinois Tool Works. |
|||
Shear Strength | 10.3 - 13.8 MPa | 1500 - 2000 psi | |
ITW Plexus Plexusâ„¢ MA3940 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Use with craze sensitive plastics.Information provided by Illinois Tool Works. |
|||
Shear Strength | 10.3 - 12.4 MPa | 1500 - 1800 psi | |
ITW Plexus Plexusâ„¢ MA422 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.All purpose adhesive, medium open time.Information provided by Illinois Tool Works. |
|||
Shear Strength | >= 10.3 MPa | >= 1500 psi | Tensile lap, Al to Al |
Master Bond EP76M-F Electrically Conductive, Two Part Epoxy Description: Master Bond EP76M-F is a two component, nickel filled, electrically conductive epoxy system for high performance bonding, sealing, and coating formulated to cure at room temperature or .. |
|||
Shear Strength | >= 10.3 MPa | >= 1500 psi | Bond, Al to Al, After 30 days at 400°F |
Master Bond Supreme 33 High Temperature Resistant, Structural Adhesive Description: Master Bond Polymer System Supreme 33 is a unique, room temperature curing, toughened epoxy adhesive/sealant, offering high temperature resistance. This innovative system offers high bo.. |
|||
Shear Strength | 10.3 MPa | 1500 psi | Lap |
Epoxy Technology EPO-TEK® H20E-LV Electrically Conductive, Silver Epoxy Product Description: EPO-TEK® H20E-LV is a two component, 100% solids silver-filled epoxy system designed specifically for chip bonding in microelectronic and optoelectronic applications. It is a .. |
|||
Shear Strength | 10.3 MPa @Temperature -55.0 °C |
1500 psi @Temperature -67.0 °F |
Overlap, Steel Solvent Wipe; ASTM D1002-72 |
3M Scotch-Weld™ 1751 B/A Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 1751 B/A is a gray, aluminum filled, two-part, room temperature curing structural adhesive.Information provided by 3M |
|||
Shear Strength | 10.3 MPa @Temperature -55.0 °C |
1500 psi @Temperature -67.0 °F |
Aluminum Overlap; ASTM D1002 |
3M Scotch-Weld™ 183 B/A Green Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 1838 B/A is a controlled flow product. This epoxy adhesives are two-part, room temperature curing structural adhesives with high shear strengths and excellent envir.. |
|||
Shear Strength | 10.3 MPa @Temperature -55.0 °C |
1500 psi @Temperature -67.0 °F |
Aluminum Overlap; ASTM D1002 |
3M Scotch-Weld™ 183 B/A Tan Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 1838 B/A is a controlled flow product. This epoxy adhesives are two-part, room temperature curing structural adhesives with high shear strengths and excellent envir.. |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap, Fiberglass |
3M Scotch-Weld™ DP100 Plus Clear Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP100 Plus Clear is a fast setting, two-part, 1:1 mix ratio mercaptan-cured epoxy adhesive. It is a unique among fast setting mercaptan cure epoxies in that it comb.. |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap, Sanded Aluminum |
3M Scotch-Weld™ DP190 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP190 Gray is a 1:1 mix ratio similar to Scotch-Weld™ Epoxy Adhesive 2216 B/A Gray and exhibits good peel, shear and environmental aging properties.Information pro.. |
|||
Shear Strength | 10.3 MPa @Temperature -55.0 °C |
1500 psi @Temperature -67.0 °F |
Overlap |
3M Scotch-Weld™ DP190 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP190 Gray is a 1:1 mix ratio similar to Scotch-Weld™ Epoxy Adhesive 2216 B/A Gray and exhibits good peel, shear and environmental aging properties.Information pro.. |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap, PP, Cohesive Failure |
3M Scotch-Weld™ DP8010 Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8010 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of Polypropyl.. |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap, 71°C 100% RH for 14 days, Mixed Mode of AF&CF |
3M Scotch-Weld™ DP810 Black Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap, Phenolic (IPA/abrade/IPA), Substrate Failure; ASTM D1002 |
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i.. |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap, Steel; ASTM D1002-64 |
3M Scotch-Weld™ CA40H Instant Adhesive 3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. Higher viscosity version of CA40 and better void filling capabilities.Information provided by 3M |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap, Gel Coat (3/16" thick), Substrate Failure |
3M Scotch-Weld™ DP8005 Translucent Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8005 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of polypropyl.. |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap, 71°C 100% RH for 14 days, Mixed Mode of AF&CF |
3M Scotch-Weld™ DP810 Tan Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap at 20 minutes after bonding |
3M Scotch-Weld™ DP810 Tan Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 10.3 MPa @Temperature 81.0 - 83.0 °C |
1500 psi @Temperature 178 - 181 °F |
Minimum MIL-A-8623 Type III Requirement |
3M Scotch-Weld™ EC-1386 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive EC-1386 is a one-part, 100% solids, thermosetting liquid adhesive.Information provided by 3M |
|||
Shear Strength | 10.3 MPa @Temperature 81.0 - 83.0 °C |
1500 psi @Temperature 178 - 181 °F |
Stored 1 year, 22-26°C, Minimum MIL-A-8623 Type III Requirement |
3M Scotch-Weld™ EC-1386 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive EC-1386 is a one-part, 100% solids, thermosetting liquid adhesive.Information provided by 3M |
|||
Shear Strength | 10.3 MPa @Temperature -55.0 °C |
1500 psi @Temperature -67.0 °F |
Aluminum Overlap; ASTM D1002 |
3M Scotch-Weld™ 3501 B/A Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 3501 B/A Gray is a rapid room temperature curing, two-part epoxy adhesives for use in bonding many metals, wood, and a variety of plastics. Equal parts by volume ar.. |
|||
Shear Strength | 10.3 MPa @Temperature -55.0 °C |
1500 psi @Temperature -67.0 °F |
Aluminum Overlap; ASTM D1002 |
3M Scotch-Weld™ DP 3501 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP 3501 is a rapid room temperature curing, two-part epoxy adhesives for use in bonding many metals, wood, and a variety of plastics. Equal parts by volume are easi.. |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap, CRS/CRS |
3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap, Stainless Steel/Stainless Steel |
3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap, Brass/Brash |
3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 10.3 MPa | 1500 psi | Overlap, Cold Rolled Steel |
3M Scotch-Weld™ DP125 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP125 Translucent is a faster curing version of 3M Scotch-Weld Epoxy Adhesive 2216 Translucent B/A. The worklife and cure time has been reduced from hours and days .. |