Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 0.379 MPa | 55.0 psi | Plate Shear, L Direction, typ |
Hexcel® HexWeb® CR III 3/8-5056-.0007 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
Shear Strength | >= 0.379 MPa | >= 55.0 psi | Plate Shear, L Direction, min |
Hexcel® HexWeb® HRH-10 - 1/4 - 1.5 Aramid Fiber/Phenolic Resin Honeycomb Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the h.. |
|||
Shear Strength | >= 0.379 MPa | >= 55.0 psi | Plate Shear, L Direction, min, preliminary value obtained from limited testing |
Hexcel® HexWeb® HRH-10 - 3/4 - 1.5 Aramid Fiber/Phenolic Resin Honeycomb Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the h.. |
|||
Shear Strength | 0.379 MPa | 55.0 psi | Plate Shear, W Direction, typ |
Hexcel® HexWeb® HRH-10 - 3/8 - 2.0 Aramid Fiber/Phenolic Resin Honeycomb Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the h.. |
|||
Shear Strength | >= 0.379 MPa | >= 55.0 psi | Plate Shear, L Direction, min |
Hexcel® HexWeb® HRH-10 - 3/8 - 1.5 Aramid Fiber/Phenolic Resin Honeycomb Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the h.. |
|||
Shear Strength | 0.379 MPa | 55.0 psi | Overlap, Neoprene Rubber; ASTM D1002-64 |
3M Scotch-Weld™ CA5 Instant Adhesive 3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. Higher viscosity, slower setting version of CA4 for filling gaps. Meets CID A-A-3097, Type II, Clas.. |
|||
Shear Strength | 0.379 MPa | 55.0 psi | Overlap, Neoprene Rubber; ASTM D1002-64 |
3M Scotch-Weld™ CA8 Instant Adhesive 3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. Slower setting than CA7 and excellent adhesion to metals, and plastics and rubbers. Meets CID A-A-3.. |
|||
Shear Strength | 0.379 MPa | 55.0 psi | Overlap, Neoprene Rubber; ASTM D1002-64 |
3M Scotch-Weld™ CA9 Instant Adhesive 3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. Slower setting version of CA8 for wire tacking and coil terminating. Meets CID A-A-3097, Type II, C.. |
|||
Shear Strength | 0.379 MPa | 55.0 psi | Overlap, Polypropylene, 50% RH |
3M 5200 Marine Adhesive/Sealant 3M™ Marine Adhesive/Sealant 5200 is a one-part polyurethane that chemically reacts with moisture to deliver strong, flexible bonds. It has excellent adhesion to wood, gelcoat and fiberglass. It for.. |
|||
Shear Strength | 0.379 MPa | 55.0 psi | Overlap, Neoprene Rubber; ASTM D1002-64 |
3M Scotch-Weld™ CA40 Instant Adhesive 3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. Very fast setting and excellent adhesion to many substrates including flexible vinyl and EPDM rubbe.. |
|||
Shear Strength | 0.379 MPa | 55.0 psi | Overlap, Neoprene Rubber; ASTM D1002-64 |
3M Scotch-Weld™ CA40H Instant Adhesive 3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. Higher viscosity version of CA40 and better void filling capabilities.Information provided by 3M |
|||
Shear Strength | 0.379 MPa | 55.0 psi | Overlap, Neoprene Rubber; ASTM D1002-64 |
3M Scotch-Weld™ CA7 Instant Adhesive 3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. Very fast setting and excellent adhesion to metals, plastics, and rubbers.Information provided by 3.. |
|||
Shear Strength | 0.379 MPa | 55.0 psi | Overlap, Neoprene Rubber; ASTM D1002-64 |
3M Scotch-Weld™ CA4 Instant Adhesive 3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. Fast setting for a variety of plastics and rubbers.Information provided by 3M |