Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 105 - 170 MPa @Temperature 60.0 - 150 °C |
15200 - 24700 psi @Temperature 140 - 302 °F |
Average value: 135 MPa Grade Count:1 |
Overview of materials for Nylon 66, Carbon Fiber/PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Carbon Fiber/PTFE Filled". Each property range of values reported is minimum and maximum value.. |
|||
Tensile Strength, Ultimate | 30.0 - 170 MPa @Strain 1.00 - 2.00 % |
4350 - 24700 psi @Strain 1.00 - 2.00 % |
Average value: 104 MPa Grade Count:1 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Tensile Strength, Ultimate | 30.0 - 170 MPa @Temperature -20.0 - 150 °C |
4350 - 24700 psi @Temperature -4.00 - 302 °F |
Average value: 104 MPa Grade Count:1 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Tensile Strength, Ultimate | 35.9 - 170 MPa | 5200 - 24700 psi | Average value: 62.9 MPa Grade Count:84 |
Overview of materials for Nylon 66, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, PTFE Filled". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Tensile Strength, Ultimate | 105 - 170 MPa @Temperature 60.0 - 150 °C |
15200 - 24700 psi @Temperature 140 - 302 °F |
Average value: 136 MPa Grade Count:1 |
Overview of materials for Nylon 66, 40% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Carbon Fiber Filled". Specific grades with carbon fiber content between 35% and 44% are in.. |
|||
Tensile Strength, Ultimate | 50.0 - 170 MPa @Temperature -40.0 - 120 °C |
7250 - 24700 psi @Temperature -40.0 - 248 °F |
Average value: 83.0 MPa Grade Count:2 |
Overview of materials for Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant". Each property range of values re.. |
|||
Tensile Strength, Ultimate | 67.6 - 170 MPa | 9800 - 24700 psi | Average value: 141 MPa Grade Count:54 |
Overview of materials for Polyethylene Terephthalate (PET), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 30% Glass Reinforced". Specific grades with glass content between 25% .. |
|||
Tensile Strength, Ultimate | 20.0 - 170 MPa @Temperature -40.0 - 121 °C |
2900 - 24700 psi @Temperature -40.0 - 250 °F |
Average value: 70.7 MPa Grade Count:7 |
Overview of materials for Nylon 6, 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% are included. .. |