Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 55.0 - 105 MPa @Temperature 60.0 - 150 °C |
7980 - 15200 psi @Temperature 140 - 302 °F |
Average value: 59.8 MPa Grade Count:3 |
Overview of materials for Polyphthalamide (PPA), 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are.. |
|||
Tensile Strength, Ultimate | 62.1 - 105 MPa | 9000 - 15200 psi | Average value: 80.6 MPa Grade Count:8 |
Overview of materials for Polycarbonate/PET Polyester Blend, Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/PET Polyester Blend, Glass Reinforced". Each property range of values reported is minimum .. |
|||
Tensile Strength, Ultimate | 10.0 - 105 MPa @Temperature 60.0 - 150 °C |
1450 - 15200 psi @Temperature 140 - 302 °F |
Average value: 50.2 MPa Grade Count:6 |
Overview of materials for Nylon 6, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Ultimate | 38.0 - 105 MPa | 5510 - 15200 psi | Average value: 70.9 MPa Grade Count:17 |
Overview of materials for Nylon 6, 20% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are includ.. |
|||
Tensile Strength, Ultimate | 60.0 - 105 MPa | 8700 - 15200 psi | Average value: 84.8 MPa Grade Count:3 |
Overview of materials for Nylon 66/6, 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are incl.. |
|||
Tensile Strength, Ultimate | 90.0 - 105 MPa @Temperature 130 - 175 °C |
13100 - 15200 psi @Temperature 266 - 347 °F |
Average value: 88.6 MPa Grade Count:5 |
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Tensile Strength, Ultimate | 90.0 - 105 MPa @Time 1.80e+7 - 7.20e+7 sec |
13100 - 15200 psi @Time 5000 - 20000 hour |
Average value: 88.6 MPa Grade Count:5 |
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Tensile Strength, Ultimate | 47.0 - 105 MPa | 6820 - 15200 psi | Average value: 80.2 MPa Grade Count:72 |
Overview of materials for Nylon 66, 40% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Mineral Filled". Specific grades with primary filler content between 35% and 44% are inclu.. |
|||
Tensile Strength, Ultimate | 45.0 - 105 MPa | 6530 - 15200 psi | Average value: 69.6 MPa Grade Count:8 |
Overview of materials for Nylon 66/6, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, Mineral Reinforced". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Ultimate | 13.0 - 105 MPa | 1890 - 15200 psi | Average value: 28.7 MPa Grade Count:73 |
Overview of materials for Polypropylene with 10% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Talc Filler". Specific grades with primary filler content between 5% and 14% are .. |
|||
Tensile Strength, Ultimate | 45.0 - 105 MPa | 6530 - 15200 psi | Average value: 57.6 MPa Grade Count:21 |
Overview of materials for Polybutylene Terephthalate (PBT), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Mineral Filled". Each property range of values reported is minimum and.. |
|||
Tensile Strength, Ultimate | 75.0 - 105 MPa | 10900 - 15200 psi | ASTM D638-68 |
Budd DSM-949, Diesel Grade SMC, Vinyl Ester, Black
(discontinued **) Used for parts requiring high strength at room temperature, good retention of properties at high temperatures and corrosion resistance, such as diesel engine external body parts.Data provided by the.. |