Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | DIN 53455; ASTM D638 |
Kolon SPELLOY® KA101 PC + PBT Alloy Resin
(discontinued **) SPELLOY® is a new technology of thermoplastic Polymer alloys developed to provide unique combination of excellent mechanical properties.High impact resistance (at low temperature), good dimensional.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Eastman Tenite Butyrate 438E0V16304 Clear, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 4%. Weight loss on heating = 0.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | DIN 53455; ASTM D638 |
Kolon Kopa® KN161 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | |
Kuraray HYBRAR® PS3 Thermoplastic Rubber-Polystyrene Blend Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
LyondellBasell Higlass SB224-2 Polypropylene Copolymer, 20% Glass Fiber Key Features: conventional melt flow, medium modulus, chemically coupled, glass fiber-reinforced polypropylene copolymer, high impact strength, moderate rigidity, good processabilityApplications: of.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 2408 Phenolic, Granular, Compression Molded PLENCO 02408 is a general purpose, organic filled phenolic molding compound, offering excellent cosmetic characteristics and improved electrical strength properties. UL recognized under component fi.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 2571 Phenolic, Granular, Transfer Molded PLENCO 02571 is a general purpose, organic filled phenolic molding compound offering optimum cure characteristics while maintaining excellent mechanical and electrical properties. UL recognized unde.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 3303 Phenolic, Granular, Compression Molded Plenco 03303 is a renumber of Plaslok 5303. Plenco 03303 is a two-stage, mineral and flock-filled phenolic molding compound offering excellent electrical insulating properties. It can be processed b.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 3356 Phenolic, Granular, Injection Molded PLENCO 03356 is a mineral filled phenolic molding compound offering excellent arc resistance, comparative tracking, and flame resistant properties. UL recognized under component file E40654. 03356 i.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 4349 Phenolic, Granular, Transfer Molded PLENCO 04349 is a heat resistant, mineral filled phenolic molding compound offering optimized cure characteristics, and excellent heat resistant properties. PLENCO 04349 is also formulated to offer .. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 6990 Phenolic, Briquette, Compression Molded PLENCO 06990 is a glass and mineral filled novolac phenolic molding compound. UL recognized under component file E40654.Information supplied by Plenco. |
|||
Tensile Strength, Ultimate | 51.0 MPa @Temperature -20.0 °C |
7400 psi @Temperature -4.00 °F |
Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 |
DuPont Elvax® 265 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Toyobo A1071D Thermoplastic Polyurethane Elastomer, Injection Grade Polybutyleneadipate type, the most general purpose type of Toyobo Polyurethane; features excellent cost-performance. Various grades of Toyobo polyurethane TPEs are used in auto parts, hoses, tubes,.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ISO 37 |
Lubrizol ESTANE® 58134 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | |
Elastomer Engineering E60D Polyurethane A polyester-based urethane with particularly high load-bearing characteristics. Information provided by Elastomer Engineering Inc (EEI) |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Eastman DURASTAR DS1010 Natural PCTA Copolyester DURASTAR DS1010 polymer contains a mold release. It has excellent appearance and clarity. Its most outstanding features are chemical resistance and excellent processing characteristics. Exposure to .. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Eastman Eastar Copolyester BR003, Natural PCTA Copolyester EASTAR BR003 Copolyester contains a mold release additive. It has excellent appearance and is nearly water-clear. Its most outstanding features are its chemical resistance and processing capabiliti.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Covestro Makroblend® EL 703 Polycarbonate + Polyester-based Blend, Impact Modified, Flame-Retardant, UV Stabilized Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboWeld 48-14/AboCure 48-14 Adhesive/Casting Resin Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboWeld 48-8/AboCure 48-8 Adhesive/Casting Resin Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | 0.5 x 0.125 in. specimen; 0.2 in/min; ASTM D638 |
Americas Styrenics STYRON™ 668 General Purpose Polystyrene Resin STYRON™ 668 is a general purpose polystyrene with medium flow and a balance of heat resistance and stiffness characteristics that make it suitable for applications such as CD jewel boxes. STYRON™.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ATSM D638 |
Ashley Polymers Ashlene® P254WO PPO A general purpose V-0 rated resin with high impact strength.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboCast 45-10/AboCure 45-10 Adhesive/Casting Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboCast 53-15/AboCure 53-15 Adhesive/Casting Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Adell ZS-10 Nylon/Olefin Alloy Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Adell ZS-30 Nylon/Olefin Alloy Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 51.0 - 240 MPa | 7400 - 34800 psi | Average value: 148 MPa Grade Count:161 |
Overview of materials for Polyetheretherketone, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Glass Fiber Filled". Each property range of values reported is minimum and maximum.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | XY; ASTM D638 |
ALM PA 614-GS Filled Nylon 12 Prototyping Polymer 40% glass sphere filled material for improved dimensional stability, increased stiffness, and higher temperature applications when compared to unfilled PA.Drop-in replacement for other commercially .. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ISO 527B |
Ineos Nova 201 Crystal Polystyrene High Heat Extrusion Grade
(discontinued **) Excellent heat resistance, Superior melt strengthApplications: Foam insulation, Oriented polystyrene sheet (OPS), XPS food packaging, Sheet and profile extrusionProperties were determined on injecti.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | 5 mm/min; parallel to flow; ASTM D638 |
Asahi Kasei Tenac®-C EF750 Acetal Copolymer, Antistat
(discontinued **) Antistatic grade containing special carbon black.Applications: Parts requiring antistatic properties.This product is not a part of the standard product line dated 2003. |