Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 490 MPa @Temperature 100 °C |
71100 psi @Temperature 212 °F |
EN min.; EN 10002-5 |
Outokumpu 4311 Cr-Ni Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.. |
|||
Tensile Strength, Ultimate | 490 MPa @Temperature 250 °C |
71100 psi @Temperature 482 °F |
EN min.; EN 10002-5 |
Outokumpu SAF 2304® Duplex Stainless Steel Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical tankersSeawater systemsFirewalls and blast walls on offshore platformsBridgesCompone.. |
|||
Tensile Strength, Ultimate | 490 MPa @Temperature 538 °C |
71100 psi @Temperature 1000 °F |
|
Kennametal Stellite Deloro® 711 PM after P/M Processing Deloro 711 is currently being developed. Adhesive wear test data: P/M 0.1, cast 0.1; Abrasive wear test data P/M 6 mm^3, cast 26 mm^3. Typical applications include vane plugs, fuel metering pins, sp.. |
|||
Tensile Strength, Ultimate | 490 MPa @Temperature 649 °C |
71100 psi @Temperature 1200 °F |
|
Kennametal Stellite Deloro® 711 PM after P/M Processing Deloro 711 is currently being developed. Adhesive wear test data: P/M 0.1, cast 0.1; Abrasive wear test data P/M 6 mm^3, cast 26 mm^3. Typical applications include vane plugs, fuel metering pins, sp.. |
|||
Tensile Strength, Ultimate | 490 MPa @Temperature 870 °C |
71100 psi @Temperature 1600 °F |
|
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Ultimate | 490 MPa | 71100 psi | |
Haynes Hastelloy® W alloy as a weld filler, base metal Type 304 Carbon steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
Tensile Strength, Ultimate | 490 MPa @Temperature 648 °C |
71100 psi @Temperature 1200 °F |
|
Haynes 556® alloy, all-weld metal GTAW Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Ultimate | 490 MPa @Temperature 538 °C |
71100 psi @Temperature 1000 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Tensile Strength, Ultimate | 490 MPa @Temperature 538 °C |
71100 psi @Temperature 1000 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Tensile Strength, Ultimate | 490 MPa @Temperature 538 °C |
71100 psi @Temperature 1000 °F |
|
Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet, GTAW weld HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Tensile Strength, Ultimate | 490 MPa | 71100 psi | Annealed prior to test |
Special Metals NILO® Alloy 36 Low-Expansion Alloy Inflection point 220°C. A nickel-iron low-expansion alloy containing 36% nickel. It maintains nearly constant dimensions over the range of normal atmospheric temperatures, and has a low coeffic.. |
|||
Tensile Strength, Ultimate | 490 MPa | 71100 psi | Annealed prior to test |
Special Metals NILO® Alloy 42 Controlled-Expansion Alloy Inflection point 370°C. A nickel-iron controlled-expansion alloy containing 42% nickel. It has a low and nominally constant coefficient of thermal expansion from room temperature to about 570Â.. |
|||
Tensile Strength, Ultimate | 490 - 560 MPa | 71100 - 81200 psi | |
SSAB Tunnplat Aluzink 420A YP High-strength Metal-coated Steel High-strength Metal-coated SteelComments: Aluzink YP - HSLA steel (aluminum-zinc coated sheet). Property values are for thicknesses 0.4 - 2.0 mm. Iron content is approximate - exact composition is .. |
|||
Tensile Strength, Ultimate | 490 - 560 MPa | 71100 - 81200 psi | |
SSAB Tunnplat Dogal 420YP High-strength Metal-coated Steel High-strength Metal-coated SteelComments: Dogal YP - HSLA steel. Property values are for thicknesses 0.4 to 2.5 mm. Iron content is approximate - exact composition is not reported by the manufactur.. |
|||
Tensile Strength, Ultimate | 490 MPa | 71100 psi | 10% Cold Worked |
AK Steel 409 ULTRA FORM® Stainless Steel AK Steel 409 ULTRA FORM Stainless Steel provides an outstanding combination of improved forming and welding characteristics, while providing superior resistance to oxidation, corrosion, ridging and .. |
|||
Tensile Strength, Ultimate | 490 MPa @Temperature 482 °C |
71100 psi @Temperature 900 °F |
|
Carpenter 20-Mo6® Stainless Steel, Tensile Properties at 93°C Data provided by Carpenter Technology Corporation.This is an austenitic stainless steel which is resistant to corrosion in hot chloride environments with low pH. It has good resistance to pitting, .. |
|||
Tensile Strength, Ultimate | 490 - 530 MPa | 71100 - 76900 psi | T direction |
ArcelorMittal Torque 20-15 Electrical Steel Properties: The iCARe™ Torque product family comes with guaranteed losses at 400Hz and indicative maximum values at 700Hz. These values are representative of the steel’s behaviour at high frequenc.. |
|||
Tensile Strength, Ultimate | 490 - 530 MPa | 71100 - 76900 psi | T direction |
ArcelorMittal Torque 27-16 Electrical Steel Properties: The iCARe™ Torque product family comes with guaranteed losses at 400Hz and indicative maximum values at 700Hz. These values are representative of the steel’s behaviour at high frequenc.. |
|||
Tensile Strength, Ultimate | 490 - 530 MPa | 71100 - 76900 psi | T direction |
ArcelorMittal Torque 30-17 Electrical Steel Properties: The iCARe™ Torque product family comes with guaranteed losses at 400Hz and indicative maximum values at 700Hz. These values are representative of the steel’s behaviour at high frequenc.. |
|||
Tensile Strength, Ultimate | 490 - 530 MPa | 71100 - 76900 psi | T direction |
ArcelorMittal Torque 30-18 Electrical Steel Properties: The iCARe™ Torque product family comes with guaranteed losses at 400Hz and indicative maximum values at 700Hz. These values are representative of the steel’s behaviour at high frequenc.. |
|||
Tensile Strength, Ultimate | >= 490 MPa | >= 71100 psi | Minimum |
ATI Allegheny Ludlum Stainless Steel AL 904L™ Alloy (UNS N08904) Allegheny Ludlum AL 904 L™ Alloy (UNS N08904) is an austenitic stainless steel alloy designed for a middles to high level of corrosion resistance. The alloy is produced to low carbon levels for us.. |
|||
Tensile Strength, Ultimate | >= 490 MPa | >= 71100 psi | |
ArcelorMittal FF 280 D Very high strength steel, Cold Rolled Steel Available in the following: HCT450X (uncoated), HCT450X+ZE (electrogalvanized) and HCT450X+Z/ZF (Extragal®/Galvannealed)Description: Dual Phase steels offer an outstanding combination of strength a.. |
|||
Tensile Strength, Ultimate | >= 490 MPa | >= 71100 psi | Minimum Guaranteed |
Industeel UREA 316L Modified 316L Mod Low Si, High Mo Stainless Steel for Urea Plants Description: UREA 316L Modified grade has been specially developed for Urea plant applications. It is a 316L modified stainless steel with extra-low silicon content and substantial higher molybdenum.. |