Polymer Property : Tensile Strength, Ultimate = 58000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	400 MPa @Temperature 400 °C	58000 psi @Temperature 752 °F	EN min.; EN 10002-5
Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and ..
Tensile Strength, Ultimate	400 MPa	58000 psi
PSM Industries Pacific Sintered Metals High Carbon Copper Steel FCC-200-P Powdered Metal High strength, Good impact resistant material for mechanical components, Excellent hardenability, High performance material with high strength and wear resistance after heat treatment Equivalent MP..
Tensile Strength, Ultimate	400 - 540 MPa	58000 - 78300 psi
Materion Beryllium Copper Alloy 25 Wire; A (TB00) Temper; 1.3-12.7 mm Diameter (UNS C17200) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to..
Tensile Strength, Ultimate	400 MPa	58000 psi
Meehanite CRS Corrosion Resisting Cast Iron Type CRS is an austenitic material with graphite in the nodular form. It conforms to ASTM designation A439-60T and provides much higher strength than type CR with excellent resistance to corrosion,..
Tensile Strength, Ultimate	400 MPa @Diameter 12.7 mm	58000 psi @Diameter 0.500 in
Kaiser 6033 T8 Rod & Bar Alloy 6033 is a higher strength version of alloy 6061, approaching properties typically obtainable with 2000 series alloys. The alloy was developed to also offer improved machinability over 6061. Th..
Tensile Strength, Ultimate	400 MPa @Temperature 870 Â°C	58000 psi @Temperature 1600 Â°F
Haynes 214Â® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	400 MPa @Temperature 300 Â°C	58000 psi @Temperature 572 Â°F	Annealed prior to test
Special Metals NILOÂ® Alloy K Controlled-Expansion Alloy Inflection point 450Â°C. A nickel-iron-cobalt controlled-expansion alloy containing 29% nickel. Its coefficient of expansion, which decreases with rising temperature to the inflection point, mat..
Tensile Strength, Ultimate	400 - 480 MPa	58000 - 69600 psi
SSAB Tunnplat DocolÂ® 400DP High-strength Steel High-strength SteelComments: Docol DP - Cold Rolled Steel - dual-phase steel. Property values are for cold-rolled steel; thicknesses 0.5 - 1.6 mm. Iron content is approximate - exact composition is..
Tensile Strength, Ultimate	400 MPa	58000 psi
Wieland 1403 Wilaform Gold Hard yellow gold alloy. Universally applicable in decoration production. Since it does not posses a very fine-grained structure it is used frequently for chainsApplications: casting, chains, lamin..
Tensile Strength, Ultimate	>= 400 MPa	>= 58000 psi
Alcoa Excalibar® 6013-T8 Aluminum, 1.9-3.8 cm diameter Weldability = A; Stress Corrosion Cracking Resistance = A; General Corrosion Resistance = B (A = best; E = worst). General 6013 characteristics and uses: High strength and good corrosion resistance...
Tensile Strength, Ultimate	400 - 503 MPa	58000 - 73000 psi
Eagle Brass 510 Phosphor Bronzes 5% A, 1/2 Hard Alloy C510 is an alloy with good strength, formability and stress relaxation characteristics, and solderability. Applications include electronic parts, springs, switches, contacts and fasteners.Info..
Tensile Strength, Ultimate	400 - 496 MPa	58000 - 72000 psi
Eagle Brass 706 Copper Nickel 10%, 1/2 Hard 706 exhibits excellent corrosion resistance, especially in marine applications. It has a relatively high strength and has resistance at elevated temperatures. The cost is relatively high compared to..
Tensile Strength, Ultimate	400 - 496 MPa	58000 - 72000 psi
Eagle Brass 752 Nickel Silver 18%, 1/4 Hard Alloy C752 combines corrosion resistance with strength and a lustrous silver color. Applications include optical frames and parts, springs, surgical instruments, jewelry, resistors and contacts.Info..
Tensile Strength, Ultimate	<= 400 MPa	<= 58000 psi
CLAL-MSX ARCAP Anticorrosion AP1 0 Annealed, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin..
Tensile Strength, Ultimate	<= 400 MPa	<= 58000 psi
CLAL-MSX NICLAL 3444 0 Annealed Copper Alloy, Free Cutting Bronze Main Characteristics: Excellent machineabilityHigh mechanical propertiesSelf lubricating alloyTypical Applications:Parts for connectorsFriction partsBearings-Pinions-Lock pinsInformation provided b..
Tensile Strength, Ultimate	400 MPa	58000 psi	annealed
CMW® ELKONIUM 76 gold based alloy Pure gold has complete resistance to atmospheric tarnish and oxidation. It does not contribute to polymer formations like platinum and palladium alloys. Wrought gold metal is very soft and prone to ..
Tensile Strength, Ultimate	400 - 460 MPa	58000 - 66700 psi
ArcelorMittal IF 300 High strength IF steel, Cold rolled Available in the following: Extragal®/Galvannealed (HX300YD+Z/+ZF)Description: These steels were designed to provide an excellent combination of drawability and mechanical strength based on their ..
Tensile Strength, Ultimate	>= 400 MPa	>= 58000 psi
AK Steel ASTM A 568 and A 635 Hot Rolled Carbon Steel, Structural Steel (SS) For conversion to A36 plateInformation provided by AK Steel
Tensile Strength, Ultimate	400 - 480 MPa	58000 - 69600 psi
ArcelorMittal H 360 Solid solution steel, Cold rolled Available in the following: uncoated (HC300P) and electrogalvanized (HC300P+ZE) Description: Solid solution steels are designed to provide high strength while maintaining good drawability. These ste..
Tensile Strength, Ultimate	400 MPa @Temperature 871 °C	58000 psi @Temperature 1600 °F
Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..