Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 380 MPa @Temperature 300 °C |
55100 psi @Temperature 572 °F |
EN min.; EN 10002-5 |
Outokumpu 4401 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r.. |
|||
Tensile Strength, Ultimate | 380 MPa @Temperature 400 °C |
55100 psi @Temperature 752 °F |
EN min.; EN 10002-5 |
Outokumpu 4401 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r.. |
|||
Tensile Strength, Ultimate | 380 - 510 MPa | 55100 - 74000 psi | |
Materion Brush 1915â„¢ Hard Temper Rod, 0.050" - 0.375" Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: as suppliedBrush 1915â„¢ is Brush Wellman's new heat-treatable leaded copper alloy. Engineered spe.. |
|||
Tensile Strength, Ultimate | >= 380 MPa | >= 55100 psi | |
Misumi Z3234 Chromium Copper Excellent mechanical strength and abrasion resistance at high temperatures. Used in welding electrodes, seam welding wheels, switch gears, electrode holder jaws, cable connectors, current carrying a.. |
|||
Tensile Strength, Ultimate | >= 380 MPa | >= 55100 psi | |
MetalTek MTEK 29-4 Cast UNS J92605 Heat Resistant Stainless Steel Restrict to low stress applications. Resists oxidation and high sulfur flue gas.Applications: Tuyeres, gas dampers, salt pots, support skids.Information provided by MetalTek |
|||
Tensile Strength, Ultimate | <= 380 MPa | <= 55100 psi | |
SSAB Tunnplat Aluzink F30A Metal-coated Mild Steel Metal-coated Mild SteelComments: Aluzink - Aluminum-zinc coated sheet. Property values are for thicknesses 0.4 - 2.00 mm. Iron content is approximate - exact composition is not reported by the manu.. |
|||
Tensile Strength, Ultimate | 380 - 460 MPa | 55100 - 66700 psi | |
SSAB Tunnplat Dogal 260 RP High-strength Metal-coated Steel High-strength Metal-coated SteelComments: Dogal RP - rephosphorized. Iron content is approximate - exact composition is not reported by the manufacturer.Data provided by SSAB Tunnplat. |
|||
Tensile Strength, Ultimate | >= 380 MPa | >= 55100 psi | |
SSAB Tunnplat Domex® 310YP Cold-forming Steel, HSLA Cold-forming Steel, HSLACharacteristics: Domex® is the brand name of hot rolled products from SSAB Tunnplat. Domex® cold-forming steels are modern structural steels. General use of Domex®.. |
|||
Tensile Strength, Ultimate | >= 380 MPa | >= 55100 psi | |
AK Steel ASTM A 463 / SAE J1392 040 AHK, Grade 40 Aluminized Carbon Steel, Structural Steel (SS) Aluminized Type 1 coating contains approximately 91% aluminum and 9% silicon that is metallurgically bonded to the low-carbon steel substrate.Information provided by AK Steel |
|||
Tensile Strength, Ultimate | >= 380 MPa | >= 55100 psi | |
AK Steel ASTM A 570, Grade 40 Hot Rolled Carbon Steel, Structural Quality (SQ) For gauges up to 0.229", ASTM A 570 must be specified, gauges >0.230", ASTM A 907 must be used. Items 0.180 to 0.230" gauge which are >48" wide may be ordered to either A 570 or A 907.Information p.. |
|||
Tensile Strength, Ultimate | >= 380 MPa | >= 55100 psi | |
AK Steel Formable, Grade 40K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA) AK Steel Formable Grade - K indicates killed.Information provided by AK Steel |
|||
Tensile Strength, Ultimate | >= 380 MPa | >= 55100 psi | |
AK Steel ZINCGRIP® ELECTRASMOOTH® Electrogalvanized Carbon Steel, HSLAS, FORMABLE 40K / SAE J1392 040 XLK or 040 YLK Information provided by AK Steel |
|||
Tensile Strength, Ultimate | >= 380 MPa | >= 55100 psi | |
AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, High Strength Low Alloy Steel (HSLA), 045XLK SAE Specified properties not covered by ASTMInformation provided by AK Steel |
|||
Tensile Strength, Ultimate | 380 MPa @Temperature 100 °C |
55100 psi @Temperature 212 °F |
Typical, after 10,000 hours |
Aleris Weldural Aluminum Alloy, 100 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||
Tensile Strength, Ultimate | 380 - 440 MPa | 55100 - 63800 psi | |
ArcelorMittal H 260 Solid solution steel, Cold rolled Available in the following: uncoated (HC260P) and electrogalvanized (HC260P+ZE) Description: Solid solution steels are designed to provide high strength while maintaining good drawability. These ste.. |