Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | >= 290 MPa | >= 42100 psi | |
H.C. Starck MoCu 70/30 Molybdenum-Copper Composite Material Description of Product: Molybdenum-copper composite materials are produced by copper infiltration of porous sintered molybdenum. They are available with different copper contents (15 - 35 %). A t.. |
|||
Tensile Strength, Ultimate | 290 MPa @Temperature 980 °C |
42100 psi @Temperature 1800 °F |
|
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Ultimate | 290 MPa @Temperature 870 °C |
42100 psi @Temperature 1600 °F |
|
Haynes Hastelloy® W alloy as a weld filler, base metal Multimet alloy 12.7 mm plate weldment Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
Tensile Strength, Ultimate | 290 MPa @Temperature 980 °C |
42100 psi @Temperature 1800 °F |
|
Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Tensile Strength, Ultimate | 290 MPa @Temperature 870 °C |
42100 psi @Temperature 1600 °F |
|
Haynes Hastelloy® alloy X 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
Tensile Strength, Ultimate | 290 MPa | 42100 psi | ACMA Test #4 |
CoorsTek Zirconia-Toughened Alumina, ZTA Thermal Shock Delta Tc = 300°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
Tensile Strength, Ultimate | 290 MPa | 42100 psi | Worked |
CMW® D510F Silver Nickel Contact Material ASTM B693 For electrical contacts.Information provided by CMW Inc. |
|||
Tensile Strength, Ultimate | >= 290 MPa | >= 42100 psi | |
AK Steel Grade 25 Cold Rolled Carbon Steel, Structural Steel (SS) Information provided by AK Steel |
|||
Tensile Strength, Ultimate | 290 MPa | 42100 psi | |
Ametek Ultra 303L P/M Stainless Steel, Sintered from 6.35 g/cc Green Density Ametek's patented Ultra Stainless Steels™ are produced by alloying the conventional austenitic compositions with a small amount of a copper-nickel-tin alloy. This results in a marked improvement i.. |
|||
Tensile Strength, Ultimate | 290 MPa | 42100 psi | Rm |
ALIMEX ACP 5080 Aluminum Cast Plate ACP 5080 is a 5xxx series precision aluminum cast plate. Thickness, flatness and surface finish offer very tight tolerances.Material stability and excellent processing characteristics make this alum.. |
|||
Tensile Strength, Ultimate | 290 MPa | 42100 psi | |
Ametek Ultra 304L P/M Stainless Steel, Sintered from 6.38 g/cc Green Density Ametek's patented Ultra Stainless Steels™ are produced by alloying the conventional austenitic compositions with a small amount of a copper-nickel-tin alloy. This results in a marked improvement i.. |
|||
Tensile Strength, Ultimate | 290 MPa @Thickness 5.00 - 12.0 mm |
42100 psi @Thickness 0.197 - 0.472 in |
Typical L-T Direction |
Aleris HOGAL 5558 Aluminum 5026 H14/H34 HOGAL 5558 is produced according to EN AW-5026.Information provided by Aleris. |
|||
Tensile Strength, Ultimate | 290 MPa | 42100 psi | Rm |
ALIMEX ACP 5080R Aluminum Cast Material Sizes range availability along with good mechanical and physical properties of ACP 5080R provide the Mold Tool Industry tooling materials solutions for the most challenging applications.Information .. |