Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 27.6 - 145 MPa | 4000 - 21000 psi | Average value: 55.7 MPa Grade Count:33 |
Overview of materials for Polybutylene Terephthalate (PBT), Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Impact Grade". Each property range of values reported is minimum and m.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | Average value: 34.4 MPa Grade Count:11 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "ABS + Glass Blend". Each property range of values reported is minimum and maximum values of appropriate .. |
|||
Tensile Strength, Ultimate | 27.6 - 186 MPa | 4000 - 27000 psi | Average value: 139 MPa Grade Count:22 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Tensile Strength, Ultimate | >= 27.6 MPa | >= 4000 psi | Reinforced |
Natural Rubber, Not Vulcanized (NR, IR, Polyisoprene) Natural rubber is polyisoprene. Chemical and environmental resistance and mechanical properties are improved through crosslinking (vulcanizing), usually through treatment with sulfur.Natural rubber.. |
|||
Tensile Strength, Ultimate | >= 27.6 MPa | >= 4000 psi | ISO 1184-1983E |
LyondellBasell Montell 8340 Polybutene-1 Key Features: semi-crystalline low ethylene content random copolymer, miscible with polypropylenes, FDA acceptableApplications: minor additive in a polyethylene peel seal layerMeets FDA requirements.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | 2 in/min.; ASTM D638 |
Ineos K44-06-122 HDPE HDPE K44-06-122 is a natural high density polyethylene copolymer designed specifically for extrusion of potable water, industrial, and mining pipe. It is recognized by the Plastic Pipe Institute as .. |
|||
Tensile Strength, Ultimate | >= 27.6 MPa | >= 4000 psi | ISO 1184-1983E |
LyondellBasell DP 0110M Polybutene Key Features: highly isotactic, semi-crystalline nucleated homopolymer, good creep resistance, good environmental stress crack resistance, FDA acceptable, easily dispersibleApplications: packaging i.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | Machine direction |
Spartech Royalstatâ„¢ R671 ABS Static Control Sheet Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
Eastman Tenite Propionate 380A2R30018 Natural, Trsp Cellulose Acetate Propionate Plasticizer 18%. Weight loss on heating = 1% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pro.. |
|||
Tensile Strength, Ultimate | 27.6 MPa @Temperature 927 °C |
4000 psi @Temperature 1700 °F |
|
Crucible Steel 430 Chromium Steel Crucible 430 is essentially a non-hardenable chromium steel which is adaptable for general purpose corrosion and heat resisting applications. It is prone to slight hardening by heat treatment. This.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
Buckeye Polymers BP PPC 0212 R Reprocessed Polypropylene, Unfilled Blk/WhiteThis reprocessed product is successful in applications where cost is a major specification, yet physical characteristics require product performance. Industrial recycled resin compounds ar.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | |
Bulk Molding Compounds BMC 100 Thermoset Polyester, GP BMC 100 is a high strength, low shrink general purpose molding compound. It can be supplied in bulk or extruded in pre-weighted slugs. Due to the excellent flow and controlled reactivity, BMC 100 is.. |
|||
Tensile Strength, Ultimate | 27.6 - 48.3 MPa | 4000 - 7000 psi | |
Bulk Molding Compounds BMC 605LWR Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 605LWR is a mineral filled, glass fiber reinforced polyester bulk molding compound suitable for compression, transfer and stuffer injection molding. It is designed to provide improved wear resis.. |
|||
Tensile Strength, Ultimate | 27.6 - 34.5 MPa | 4000 - 5000 psi | |
Bulk Molding Compounds BMC 902 Thermoset Polyester, Soft Flow Encapsulation Grade BMC 902 is a medium strength, high flow molding compound that meets Ford Specification ESFM3D114- A. BMC 902 has excellent electrical properties and creep resistance. It can be pigmented in a wide r.. |
|||
Tensile Strength, Ultimate | 27.6 - 34.5 MPa | 4000 - 5000 psi | |
Bulk Molding Compounds BMC SLC 1000 Glass Reinforced Polyester BMC SLC 1000 is a medium strength, low-cost, glass reinforced polyester compound with adjustable shrinkage. It is V-0 flame arc and track resistant. UL® recognized. This material was formerly known.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
Buckeye Polymers BP RPP 2006 T Polypropylene, 20% Mineral Filled This Talc-filled product exhibits excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and mar resistance, and resis.. |
|||
Tensile Strength, Ultimate | 27.6 - 48.3 MPa | 4000 - 7000 psi | |
Bulk Molding Compounds BMC 1100 Corelyn Glass Fiber Reinforced Polyester Compound BMC 1100, also known as CoreLyn, is a food contact safe material with excellent scratch and stain resistant properties. CoreLyn can be pigmented to match virtually any color. This glass fiber-reinfo.. |
|||
Tensile Strength, Ultimate | 27.6 - 34.5 MPa | 4000 - 5000 psi | |
Bulk Molding Compounds BMC 1410 Electrical Grade BMC 1410 is a high-strength electrical grade material with excellent flammability resistance. In most applications, this material is competitive with SMC. Equal performance at a lower cost. Normally.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | |
Bulk Molding Compounds BMC 200 Thermoset Polyester, Electrical Grade BMC 200 is a high strength, low shrink molding compound. It can be supplied in bulk or extruded in pre-weighted slugs.Typical applications are circuit breakers, insulators, bobbins, electrical conne.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | ASTM D638 |
Arkema Group Kynar Super Flex® 2500 PVDF Copolymer
(discontinued **) Copolymer Series, Kynar® components are used extensively in the high purity semiconductor market, the pulp and paper industry, nuclear waste processing, and the general chemical processing industry.. |
|||
Tensile Strength, Ultimate | 27.6 - 124 MPa | 4000 - 18000 psi | Average value: 83.6 MPa Grade Count:99 |
Overview of materials for Polycarbonate, Glass + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass + PTFE Filled". Each property range of values reported is minimum and maximum value.. |
|||
Tensile Strength, Ultimate | 27.6 - 31.0 MPa | 4000 - 4500 psi | TM R050-36 |
Resinlab® EP1195 Flame Retardant Epoxy Casting Resin Resinlab™ EP1195 is a low viscosity, fast gelling, flame retardant epoxy casting resin system. It is recognized under the Component Recognition Program of Underwriters Laboratories Inc., (File # E1.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | TM R050-36 |
Resinlab® EP1300 Black Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1300 Black (Formerly Lab Product W092602) is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It has a pot life of about one hour and .. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 40S Chlorosulfonated Polyethylene Rubber, General Description
(discontin Product form is white, odorless chips. Distinguishing Feature: Low viscosity polymer. Improves processing of dry stiff stocks.35 % Chlorine Content. 1% Sulfur Content. Excellent Abrasion Resista.. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, General Description
(discontinu Product form is white, odorless chips. Distinguishing Feature: Medium polymer viscosity. Versatile.35 % Chlorine Content. 1% Sulfur Content. Excellent Abrasion Resistance. Excellent Chemical Re.. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 4085 Chlorosulfonated Polyethylene Rubber, General Description
(disconti Product form is white, odorless chips. Distinguishing Feature: High polymer viscosity. Good green strength. Improves processing of soft or highly extended stocks.36 % Chlorine Content. 1% Sulfur.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | TM R050-36 |
Resinlab® EP1046FG Clear Electronic Grade Epoxy Encapsulant Resinlab™ EP1046FG Clear is a two part unfilled very fast curing electronic grade epoxy encapsulant designed for small castings (less than 25 grams). It cures very quickly with low exotherm to a to.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
Buckeye Polymers BP RPP 2007 TR Blk Reprocessed Polypropylene, 20% Mineral Filled Talc Filled BlackThis reprocessed product is successful in applications where cost is a major specification, yet physical characteristics require product performance. Industrial recycled resin comp.. |