Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 2000 MPa | 290000 psi | Fiber only. Composites containing this fiber may have tensile strength of 1000 MPa. |
Type P-VSB-32 (Union Carbide) Carbon Fiber Pitch fibers are prepared by heating aromatic compounds above 350°C. A dehydrogenation condensation reaction occurs to form planar aromatic molecules which aggregate into a liquid crystalline phas.. |
|||
Tensile Strength, Ultimate | 2000 MPa | 290000 psi | Fiber only. Composites containing this fiber may have tensile strength of 1000 MPa. |
Type P-VS-0053 (Union Carbide) Carbon Fiber Pitch fibers are prepared by heating aromatic compounds above 350°C. A dehydrogenation condensation reaction occurs to form planar aromatic molecules which aggregate into a liquid crystalline phas.. |
|||
Tensile Strength, Ultimate | 2000 MPa | 290000 psi | |
China Tungsten YG9X Tungsten Carbide Powder Information provided by China Tungsten |
|||
Tensile Strength, Ultimate | 2000 MPa @Thickness 25.4 mm |
290000 psi @Thickness 1.00 in |
filament |
3M Nextel™ 440 Industrial Ceramic Fiber Chemical composition above is wt%. Crystal phases are gamma alumina + mullite + amorphous SiO2. Filament diameter is 10-12 µm.3M Nextel fibers 312, 440, and 550 are designed for non-structural ap.. |
|||
Tensile Strength, Ultimate | 2000 MPa @Thickness 25.4 mm |
290000 psi @Thickness 1.00 in |
gauge filament |
3M Nextel™ 550 Industrial Ceramic Fiber Chemical composition above is wt%. Crystal phases are gamma alumina amorphous SiO2. Filament diameter is 10-12 µm.3M Nextel fibers 312, 440, and 550 are designed for non-structural applications w.. |