- Polymer Property : Tensile Strength, Ultimate = 10900 psi
Polymer Property : Tensile Strength, Ultimate = 10900 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 75.0 - 193 MPa | 10900 - 28000 psi | Average value: 93.5 MPa Grade Count:13 |
| Overview of materials for Polyetheretherketone, PEEK, Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PEEK, Aramid Fiber Filled". Each property range of values reported is minimum and .. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | |
| Polycasa Acryl® G 88 E Acrylic Same as Lucryl G 88, but higher resistance to stress cracking and higher processing viscosity. Used for: extruded protective layer on PVC, ABS and PC for outdoor applications, as well as bath tubs .. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ISO 527 |
| LATI LARIL 13 G/10 10% Glass Fiber Reinforced Polyphenylene Oxide (PPOm)
(discontinued **) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ASTM D638 |
| Quantum Composites QC-2130 Phenolic 25% Glass Fiber SMC
(discontinued **) QC-2130 is a glass-reinforced sheet molding compound based on a phenolic resin matrix. It exhibits outstanding low flammability characteristics. QC-2130 is recommended for applications such as air.. |
|||
| Tensile Strength, Ultimate | 75.0 - 353.701 MPa @Temperature -40.0 - 150 °C |
10900 - 51300.1 psi @Temperature -40.0 - 302 °F |
Average value: 147 MPa Grade Count:4 |
| Overview of materials for Nylon 66, 60% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. .. |
|||
| Tensile Strength, Ultimate | 75.0 - 320 MPa | 10900 - 46400 psi | Average value: 179 MPa Grade Count:43 |
| Overview of materials for Nylon 66, 10% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Carbon Fiber Filled". Specific grades with carbon fiber content between 5% and 14% are inc.. |
|||
| Tensile Strength, Ultimate | 75.0 - 222 MPa | 10900 - 32200 psi | Average value: 145 MPa Grade Count:80 |
| Overview of materials for Nylon 610, Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610, Glass Reinforced". Each property range of values reported is minimum and maximum values of ap.. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ASTM data at 5 mm/min. |
| BASF Capron® 1202CQ Nylon 6 (Dry)
(discontinued **) Capron 1202CQ is a blended low viscosity, polyamide 6 injection molding homopolymer, possessing a modified crystalline structure for increased property performance and faster cycles. It is also ava.. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ASTM data at 5 mm/min. |
| BASF Capron® 8202 NL Nylon 6 (Dry)
(discontinued **) Capron 8202 NL is an unfilled, low viscosity, non-lubricated nylon 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is available in natural, heat sta.. |
|||
| Tensile Strength, Ultimate | 75.0 MPa @Temperature 22.0 °C |
10900 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Menzolit Menzolit® SMC 2600 Unsaturated Polyester UP SMC 2600 is a special SMC with electrically conductive properties. Because of its conductivity, SMC 2600 is antistatic and prevents build-up of electrical charges on the surface. Despite of its cond.. |
|||
| Tensile Strength, Ultimate | 75.0 MPa @Temperature 22.0 °C |
10900 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Menzolit Menzolit® SMC 0420 Unsaturated Polyester UP SMC 0420 is a low density Premium Class-A SMC for exterior body applications on cars, LCV´s and trucks. These compounds mould to light weight parts with good up to excellent surface quality for .. |
|||
| Tensile Strength, Ultimate | 75.0 MPa @Temperature 22.0 °C |
10900 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Menzolit Menzolit® SMC 0421 Unsaturated Polyester UP SMC 0421 is a low density premium Class-A SMC for on-line painted exterior body applications on cars. These compounds mould to light weight parts with excellent surface quality for on-line painted .. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | |
| Sapco C 220 Steatite Information provided by Sapco. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | |
| Sapco C 221 Steatite Information provided by Sapco. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ISO 527 |
| Wellman Wellamid® GS40-66 22L-N 40% Glass Sphere Filled Nylon 66, Lubricated Typical Applications: Potentiometer liners, electrical coil forms, automotive window lift and power door lock switch bodies, gears, thick wall section moldings, emission control valves.Data provided.. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ISO 527 |
| Wellman Wellamid® MR259 22LH-N 25% Mineral Reinforced Nylon 66, Lubricated & Heat Stabilized Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co.. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ISO 527 |
| Wellman Wellamid® T423-BK10 Mineral Reinforced Nylon 6, Heat Stabilized Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co.. |
|||
| Tensile Strength, Ultimate | 75.0 - 97.0 MPa | 10900 - 14100 psi | ASTM D638 |
| Zeus PEEK Tubing PEEK (polyetheretherketone) is a high-performance engineered polymer with excellent endurance to heat and one of the highest strength-to-weight ratios of any thermoplastic. This material can be used.. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | |
| Covestro Baygal® 90 IK 69 Polyurethane Uses: Suitable for impregnation and encapsulation of coils, especially when high heat deflection temperature, and eventually fire resistance is requested.Information provided by Bayer.As of 1 Septem.. |
|||
| Tensile Strength, Ultimate | 75.0 MPa @Temperature 180 °C |
10900 psi @Temperature 356 °F |
ISO 527-1/-2 |
| DSM Stanyl® OCD2100 BK27021 PA46-GF40 40% Glass Reinforced, Heat Stabilized |
|||
| Tensile Strength, Ultimate | 75.0 MPa @Temperature 180 °C |
10900 psi @Temperature 356 °F |
ISO 527-1/-2 |
| DSM Stanyl® OCD2300 BLK PA46-GF50 50% Glass Reinforced, Heat Stabilized |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | |
| BASF Luranyl® KR 2454/3 G2 Polyphenylene Ether + Styrene-Butadiene Blend, 10% Glass Fiber Reinforced Heat resistant grade with halogen-free flame retardant; applications include TV plug connectors and components in switchgear cabinets.Data was collected by ISO methods and provided by BASF. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ATSM D638 |
| Ashley Polymers Ashlene® 630 Nylon 6, General Purpose A general purpose Nylon 6 resin for injection molding.Data provided by the manufacturer |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ISO R527 |
| Arkema Group Orgalloy® RS 6015 ES T6L Polyamide Alloy Polyamide Alloy, Blow Molding of Technical PartsInformation provided by Arkema Group |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | |
| BASF Luranyl® KR 2403 G2 Polyphenylene Ether + Styrene-Butadiene Blend, 10% Glass Fiber Reinforced General-purpose grade with 10% glass fiber for parts requiring especially good resistance to heat deformation.Applications: auto parts, steering-column cladding and water meters.Data was collected b.. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 |
| Lucite International Perspex™ GS Acrylic Cast Sheet 000/0000 PERSPEX cast sheet is made between sheets of high quality glass and produced in batches. It has a very high molecular weight making it strong, resilient and easy to handle and fabricate. The cast me.. |
|||
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ASTM D638 |
| Sumitomo Bakelite North America FM 4005 Fiberglass Reinforced Phenolic Novolac FM 4005 is a fiberglass reinforced phenolic novolac molding compound, with excellent dimensional stability and good strength at elevated temperatures. This material is compliant with the specificat.. |
|||
| Tensile Strength, Ultimate | 75.0 - 105 MPa | 10900 - 15200 psi | ASTM D638-68 |
| Budd DSM-949, Diesel Grade SMC, Vinyl Ester, Black
(discontinued **) Used for parts requiring high strength at room temperature, good retention of properties at high temperatures and corrosion resistance, such as diesel engine external body parts.Data provided by the.. |
|||
| Tensile Strength, Ultimate | 75.0 - 88.0 MPa | 10900 - 12800 psi | Average value: 82.3 MPa Grade Count:3 |
| Overview of materials for Thermoset Polyurethane, Liquid, Quartz Filled This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Liquid, Quartz Filled". Each property range of values reported is minimum and ma.. |
|||