Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 28.42 - 60.0 MPa @Temperature 70.0 - 100 °C |
4122 - 8700 psi @Temperature 158 - 212 °F |
Average value: 46.5 MPa Grade Count:6 |
Overview of materials for Thermoplastic Polyurethane, Elastomer, Ether Grade This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane, Elastomer, Ether Grade". Each property range of values reported is minimum a.. |
|||
Tensile Strength, Ultimate | 28.42 - 60.0 MPa @Time 0.000 - 4.84e+6 sec |
4122 - 8700 psi @Time 0.000 - 1340 hour |
Average value: 46.5 MPa Grade Count:6 |
Overview of materials for Thermoplastic Polyurethane, Elastomer, Ether Grade This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane, Elastomer, Ether Grade". Each property range of values reported is minimum a.. |
|||
Tensile Strength, Ultimate | 15.0 - 60.0 MPa @Temperature 60.0 - 120 °C |
2180 - 8700 psi @Temperature 140 - 248 °F |
Average value: 36.7 MPa Grade Count:1 |
Overview of materials for Polyphenylene Ether, 10% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 10% Glass Filled". Specific grades with glass content between 5% and 14% are includ.. |
|||
Tensile Strength, Ultimate | 8.00 - 60.0 MPa @Temperature 60.0 - 90.0 °C |
1160 - 8700 psi @Temperature 140 - 194 °F |
Average value: 29.6 MPa Grade Count:3 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Tensile Strength, Ultimate | 40.0 - 60.0 MPa | 5800 - 8700 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 3108/0903 Anti-static PVDF Compound
(discontinued **) Key features of this grade: Anti-static, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crystall.. |
|||
Tensile Strength, Ultimate | 40.0 - 60.0 MPa | 5800 - 8700 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 3208/0150 Anti-friction PVDF Compound
(discontinued **) Key features of this grade: Anti-friction, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crysta.. |
|||
Tensile Strength, Ultimate | 37.0 - 60.0 MPa | 5370 - 8700 psi | Average value: 51.9 MPa Grade Count:21 |
Overview of materials for Phenolic, Novolac, Mineral/Flock Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Flock Filled". Each property range of values reported is minimum and maximum .. |
|||
Tensile Strength, Ultimate | 39.3 - 60.0 MPa | 5700 - 8700 psi | Average value: 53.1 MPa Grade Count:3 |
Overview of materials for Nylon 6/69 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6/69". Each property range of values reported is minimum and maximum values of appropriate MatWeb .. |
|||
Tensile Strength, Ultimate | 50.0 - 60.0 MPa | 7250 - 8700 psi | ASTM D638 |
Chang Chun Plastic PBT1100L General Purpose PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 50.0 - 60.0 MPa | 7250 - 8700 psi | ASTM D638 |
Chang Chun Plastic PBT1200M General Purpose PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 1.32 - 60.0 MPa | 191 - 8700 psi | Average value: 19.0 MPa Grade Count:22 |
Overview of materials for Silicone Polyurethane, Ether Based This property data is a summary of similar materials in the MatWeb database for the category "Silicone Polyurethane, Ether Based". Each property range of values reported is minimum and maximum value.. |
|||
Tensile Strength, Ultimate | 9.00 - 60.0 MPa @Temperature 60.0 - 120 °C |
1310 - 8700 psi @Temperature 140 - 248 °F |
Average value: 36.3 MPa Grade Count:4 |
Overview of materials for Polypropylene with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are i.. |