Polymer Property : Tensile Strength, Ultimate = 290 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	13.9 - 290 MPa	2010 - 42100 psi	Average value: 199 MPa Grade Count:56
Overview of materials for Polyphthalamide (PPA), 50% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 50% Glass Fiber Reinforced". Each property range of values reported is minimum and maxi..
Tensile Strength, Ultimate	75.0 - 290 MPa	10900 - 42000 psi	Average value: 188 MPa Grade Count:7
Overview of materials for Phenolic/Glass Fiber SMC This property data is a summary of similar materials in the MatWeb database for the category "Phenolic/Glass Fiber SMC". Each property range of values reported is minimum and maximum values of appro..
Tensile Strength, Ultimate	234 - 290 MPa	34000 - 42000 psi
Eagle Brass 110 EPT COPPER, 1/4 Hard Alloy 110, also known as electrolytic tough pitch (ETP) copper, is commonly used in electric current carrying applications. 110 Copper is 99.9% pure copper with an electrical conductivity rating of ..
Tensile Strength, Ultimate	248 - 290 MPa	36000 - 42000 psi
Eagle Brass 220 Commercial Bronze, Annealed CDA 220 is known for having very good corrosion resistance, great cold workability and good hot workability for drawing, blanking, coining, stamping, piercing and punching. Typical uses include plum..
Tensile Strength, Ultimate	234 - 290 MPa	34000 - 42000 psi
Eagle Brass 102 OF COPPER (Non-Certified), 1/4 Hard Alloy 102 is an oxygen-free copper which has better forming, resistance to hydrogen embrittlement, and brazing characteristics than C110 ETP. C102 has good solder-ability and corrosion resistance an..
Tensile Strength, Ultimate	234 - 290 MPa	34000 - 42000 psi
Eagle Brass 101 OFE COPPER (Certified), 1/4 Hard Alloy 101 is known as Oxygen-Free Electronic (OFE). It reaches a minimum of 101% IACS conductivity rating. It is the most expensive out of the 101- 110 group because of its higher purity.Information..