Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 3.73 - 125 MPa @Temperature -40.0 - 160 °C |
541 - 18100 psi @Temperature -40.0 - 320 °F |
Average value: 53.1 MPa Grade Count:2 |
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% .. |
|||
Tensile Strength, Ultimate | 3.73 - 125 MPa @Strain 0.250 - 10.0 % |
541 - 18100 psi @Strain 0.250 - 10.0 % |
Average value: 53.1 MPa Grade Count:2 |
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% .. |
|||
Tensile Strength, Ultimate | 97.0 - 125 MPa | 14100 - 18100 psi | Average value: 113 MPa Grade Count:15 |
Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT or PCTA, 30% Glass Reinforced".Specific grades with glass content between 25% and 34% are included. .. |
|||
Tensile Strength, Ultimate | 50.0 - 125 MPa @Temperature 0.000 - 160 °C |
7250 - 18100 psi @Temperature 32.0 - 320 °F |
Average value: 67.6 MPa Grade Count:4 |
Overview of materials for Polysulfone (PSU) This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
Tensile Strength, Ultimate | 50.0 - 125 MPa | 7250 - 18100 psi | Average value: 90.5 MPa Grade Count:6 |
Overview of materials for Phenolic, Resole, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Resole, Glass Fiber Filled". Each property range of values reported is minimum and maximum val.. |
|||
Tensile Strength, Ultimate | 110 - 125 MPa @Temperature 130 - 175 °C |
16000 - 18100 psi @Temperature 266 - 347 °F |
Average value: 128 MPa Grade Count:4 |
Overview of materials for Nylon 66, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
Tensile Strength, Ultimate | 110 - 125 MPa @Time 1.80e+7 - 7.20e+7 sec |
16000 - 18100 psi @Time 5000 - 20000 hour |
Average value: 128 MPa Grade Count:4 |
Overview of materials for Nylon 66, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
Tensile Strength, Ultimate | 89.6 - 125 MPa | 13000 - 18100 psi | Average value: 100 MPa Grade Count:8 |
Overview of materials for Polyphthalamide (PPA), 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are .. |
|||
Tensile Strength, Ultimate | 52.0 - 125 MPa @Temperature 0.000 - 160 °C |
7540 - 18100 psi @Temperature 32.0 - 320 °F |
Average value: 78.5 MPa Grade Count:2 |
Overview of materials for Polysulfone, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are inc.. |