Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 870 - 1030 MPa @Diameter 9.52 mm |
126000 - 149000 psi @Diameter 0.375 in |
CWSR; DAN 2700.9 |
Haynes Ti-3Al-2.5V Alloy Titanium Tubing Haynes® Ti-3Al-2.5V alloy is both lightweight and strong, providing a major design advantage - saving weight.Specific alloying additives, notably aluminum, raise the temperature at which a titani.. |
|||
Tensile Strength, Ultimate | 870 - 1030 MPa @Diameter 12.7 - 25.4 mm |
126000 - 149000 psi @Diameter 0.500 - 1.00 in |
CWSR; DAN 2700.9 |
Haynes Ti-3Al-2.5V Alloy Titanium Tubing Haynes® Ti-3Al-2.5V alloy is both lightweight and strong, providing a major design advantage - saving weight.Specific alloying additives, notably aluminum, raise the temperature at which a titani.. |
|||
Tensile Strength, Ultimate | 689 - 1030 MPa | 100000 - 150000 psi | |
Special Metals DURANICKEL® 301 (UNS N03301) Cold-Drawn Rod and Bar Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Cold-Drawn Rod and Bar specifically. Other property values are typical of annealed DURANICKEL®.. |
|||
Tensile Strength, Ultimate | 930 - 1030 MPa | 135000 - 149000 psi | |
CLAL-MSX NICLAFOR® 1000 TH2 Quenched/Precipitation Heat Treated, Drawn Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi.. |
|||
Tensile Strength, Ultimate | 972 - 1030 MPa | 141000 - 149000 psi | Rm |
Arcam Ti6Al4V Titanium Alloy Ti6Al4V is the most widely used titanium alloy and has numerous applications in the medical industry, aerospace, automotive and marine equipment industry. Ti6Al4V ELI features Extra Low Interstitial.. |