Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 980 MPa | 142000 psi | |
Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Tensile Strength, Ultimate | 980 MPa | 142000 psi | |
Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Tensile Strength, Ultimate | 980 MPa | 142000 psi | |
Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Tensile Strength, Ultimate | 980 MPa | 142000 psi | |
Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Ultimate | 980 - 1100 MPa | 142000 - 160000 psi | |
ArcelorMittal Dual Phase 980 LCE Y660 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft .. |
|||
Tensile Strength, Ultimate | 980 - 1200 MPa | 142000 - 174000 psi | |
ArcelorMittal Complex Phase Steel 1000 SF Very high strength steel, Cold Rolled Steel Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product range. These steels are cold formed to make lightweight structural elements. A num.. |
|||
Tensile Strength, Ultimate | 980 - 1200 MPa | 142000 - 174000 psi | |
ArcelorMittal Complex Phase Steel 1000 Very high strength steel, Cold Rolled Steel Available in the following: uncoated (HCT980C) and electrogalvanized (HCT980C+ZE)Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product r.. |
|||
Tensile Strength, Ultimate | 980 - 1130 MPa | 142000 - 164000 psi | |
ArcelorMittal Complex Phase Steel 1000 Y800 Very high strength steel, Cold Rolled Steel Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product range. These steels are cold formed to make lightweight structural elements. A num.. |
|||
Tensile Strength, Ultimate | 980 - 1100 MPa | 142000 - 160000 psi | |
ArcelorMittal Dual Phase 1180 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft .. |
|||
Tensile Strength, Ultimate | 980 - 1100 MPa | 142000 - 160000 psi | |
ArcelorMittal Dual Phase 980 LCE Y700 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft .. |
|||
Tensile Strength, Ultimate | 980 - 1100 MPa | 142000 - 160000 psi | |
ArcelorMittal Dual Phase 980 Y700 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft .. |
|||
Tensile Strength, Ultimate | 980 MPa | 142000 psi | |
Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |