Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 94.0 - 179.953 MPa @Temperature -40.0 - 120 °C |
13600 - 26100.0 psi @Temperature -40.0 - 248 °F |
Average value: 142 MPa Grade Count:3 |
Overview of materials for Polyphenylene Sulfide (PPS) with 50% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 50% Glass Fiber Filler". Specific grades with glass content between 45%.. |
|||
Tensile Strength, Ultimate | 94.0 MPa | 13600 psi | ISO 527-1, 2 |
Polyplastics Duranex® CRN7830 Polybutylene Terephthalate (PBT), Lower noise, 30% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 94.0 MPa | 13600 psi | ISO 527-1, 2 |
Polyplastics Duranex® 7400W Polybutylene Terephthalate (PBT), Super low warpage, GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 94.0 MPa | 13600 psi | ATSM D638 |
Ashley Polymers Ashlene® 527LD-13G Nylon 66, 13% Glass Reinforced A high impact 13% glass reinforced Nylon 66.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 94.0 MPa | 13600 psi | ATSM D638 |
Ashley Polymers Ashlene® 527LD-14G Nylon 66, 14% Glass Reinforced A high impact nylon with 14% glass.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 94.0 MPa | 13600 psi | ASTM D638 |
Chem Polymer Chemlon 100 W Nylon 66, MoS2 Filled A molybdenum disulfide modified nylon 66 exhibiting superior tensile strength and wear resistance, greater dimensional stability and higher heat resistance than general purpose nylon 66.Data provide.. |
|||
Tensile Strength, Ultimate | 94.0 MPa | 13600 psi | ASTM D638 |
A. Schulman ComAlloy Lubrilon® 602 Nylon 6/6, Molybdenum Disulfide Filled, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
Tensile Strength, Ultimate | 94.0 MPa | 13600 psi | ASTM D638 |
A. Schulman ComAlloy Voloy® 415 Polyester - PBT, Glass/Mineral Reinforced, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.30% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 94.0 MPa | 13600 psi | ASTM D638 |
A. Schulman ComAlloy Voloy® 612 Nylon 6, Glass Fiber/Bead Reinforced, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.30% Glass Fiber/Bead Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 94.0 MPa @Temperature 120 °C |
13600 psi @Temperature 248 °F |
ISO 527 |
LATI LARTON G/50 50% Glass Fiber Filled Polyphenylene sulfide (PPS)
(discontinued **) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |